Movement Strategy Influences on the Characteristics of Low-Carbon Steel Generated by the Lamination Object Manufacturing Method

Abstract

This paper investigates the effects of heating movement techniques on the properties of low-carbon steel samples that are 3D printed using S20C lamination object manufacturing (LOM). A Tungsten iner gas (TIG) machine and a computer numerical control (CNC) machine were used together to join the steel sheet. The LOM samples were created with a straight-profile, short-profile, cross-profile, and curved-profile. The results indicate that the majority of the samples had a grain size number of 7–9. The samples exhibited an isotropy grain shape. The LOM samples exhibited dimples, which suggests ductility fractures. Pore flaws showed up in the microstructure of the cross-profile and short-profile samples during the LOM process. The samples with curved- and straight-profiles had a better microstructure. In comparison to samples with a short profile and a cross-profile, the samples with a straight-profile and a curved-profile had a superior combination of ultimate tensile strengths (UTSs) and elongation value. The straight- and curved-profiles’ greater elongation and tensile strength can be attributed to their improved microstructure and finer grain size. A straight-profile sample with an elongation value of 25.6% and a UTS value of 430 MPa was the ideal LOM sample. Conversely, the weakest sample was the LOM sample with a cross-profile, which had an elongation value of 10.8% and a UTS value of 332.5 MPa. This research could provide further information about the LOM method and the best straight-profile movement strategy. A suitable TIG gun movement strategy could produce a good LOM sample with a good microstructure, tensile strength, and ductility. Further research should incorporate more movement strategies and techniques that completely prevent the formation of pore defects.