Moisture Transport in Loose Fibrous Insulations under Steady-State Boundary Conditions

Abstract

This research aimed to compare the transport capacity of loose-fill mineral wool, cellulose fibers, and wood wool to transfer moisture under steady-state conditions. The tests were carried out in the heat flow meter apparatus, which created a constant thermal field, limiting samples of sorptive moistened materials. The thermal conductivity, stabilization time, and moisture content of the samples were measured. Based on the variation in the results, the dynamism of moisture transport in the materials was determined. Mineral wool samples showed the lowest sorption. As a result, the moisture transport in this material stopped the fastest. In the case of cellulose and wood fibers, moisture transport continued throughout the whole test procedure. It was noted that the amount of moisture transport is influenced primarily by the structure of the fibers, the moisture content, and the possible presence of air in the pores. The wetter the material, the faster the transport. The dynamism of moisture transport according to trends of thermal conductivity changes over time was analyzed. The greater the slope of the linear regression line, the greater the dynamics of change. The smallest dynamics of change were found for mineral wool, for which the measured slope was between −0.008 and −0.033. For cellulose and wood wool, the range of slope was from −0.141 to −0.210, and from −0.162 to −0.211, respectively. The results of this research may provide the basis for further work on buffering moisture in the adjacent internal layers of the frame walls.

Practical Use of Materials of Natural Origin as Loose-Fill Insulations in Open-Diffusion Constructions—Observation and Numerical Simulation

“…All the materials were analyzed as loose-fill thermal insulations of frame walls. Most of the properties were laboratory-investigated by the authors [30,31]. Due to the loose state of the analyzed insulations, the material can be blown into the wall structure.…”

“…All the materials were analyzed as loose-fill thermal insulations of frame walls. Most of the properties were laboratory-investigated by the authors [30,31].…”

“…The individual fibers are hollow, thus creating a capillary system. Between fibers with diameters of 20-35 µm, there are spaces of 10-45 µm [31]. The dependence of the thermal conductivity coefficient of loose wood wool on density is shown in Figure 3.…”

“…The fiber surfaces are rough, with numerous protrusions, and holes. The individual fibers are hollow, thus creating a capillary system bers with diameters of 20-35 µm, there are spaces of 10-45 µm [31]. The d the thermal conductivity coefficient of loose wood wool on density is show Cellulose insulation is made from cellulose fibers by reusing used news production, newsprint is shredded and impregnated, among others, with pounds and aluminum hydroxide, as a result of which the material becom the formation of fungi and molds.…”

“…The d the thermal conductivity coefficient of loose wood wool on density is show Cellulose insulation is made from cellulose fibers by reusing used news production, newsprint is shredded and impregnated, among others, with pounds and aluminum hydroxide, as a result of which the material becom the formation of fungi and molds. Cellulose granules can be used to insulate places, insulate external and internal sandwich walls, and insulate ceilings an special pneumatic devices [31]. Long-grain papers, such as daily newspa high-circulation newspapers, are best to use.…”