Model for Periodic Analysis of the Quantity of Water Evaporated during Thermo-processing of Clay Designated for Production of Oven Refractory

Abstract

A model has been derived for periodic analysis of the quantity of water evaporated during thermo-processing of clay designated for production of oven refractory. The model; γ = exp lnt 1.3 2.9206 shows that the quantity of evaporated water during the drying process is dependent on the drying time, with the evaporating surface being constant. It was found that the validity of the model is rooted on the expression lnγ = (lnt/Logβ) N where both sides of the equation are correspondingly almost equal. The maximum deviation of the model-predicted quantity of evaporated water from the corresponding experimental value is less than 19% which is quite within the acceptable deviation range of experimental results. Water evaporation rate as obtained from experiment and derived model were evaluated to be 0.0536 and 0.0337g mins-1 respectively.

Perspective raw materials of Uzbekistan for the production of refractory materials

“…Следует отметить, что спекание огнеупорных шихт с высокоглиноземистыми компонентами, в частности гидратами глинозема или техническим глиноземом, сопровождается небольшой усадкой при их обжиге, что позволяет в некоторых случаях обходиться без стадии предварительного высокотемпературного синтеза муллита [12,13] Повышенное содержание оксидов-плавней в пробах высокоглиноземистых отходов ШГХК и шерабадской бокситоподобной породы ограничивает возможности их использования для получения заполнителей бетонов и торкрет-масс. Путем их спекания с высокоглиноземистыми отходами ШГХК были синтезированы образцы муллитового и муллитокремнеземистого составов, которые могут представлять практический интерес.…”