Microstructure and Mechanical Properties of Si3N4-Fe3Si Composites Prepared by Gas-Pressure Sintering

Abstract

Si3N4-Fe3Si composites were prepared using Fe-Si3N4 as the source of Fe3Si by gas-pressure sintering. By adding different amounts of Fe-Si3N4 into the starting powders, Si3N4-Fe3Si composites with various Fe3Si phase contents were obtained. The microstructure and mechanical properties of the composites were investigated. With the increase of Fe-Si3N4 contents, the content and particle size of Fe3Si both increased. When more than 60 wt. % Fe-Si3N4 were added, the abnormal growth of Fe3Si particles occurred and oversized Fe3Si particles appeared, leading to non-uniform microstructures and worse mechanical properties of the composites. It has been found that Fe3Si particles could toughen the composites through particle pull-out, interface debonding, crack deflection, and particle bridging. Uniform microstructure and improved mechanical properties (flexural strength of 354 MPa and fracture toughness of 8.4 MPa·m1/2) can be achieved for FSN40.