Metal–Organic Framework as an Efficient Synergist for Intumescent Flame Retardants against Highly Flammable Polypropylene

Abstract

The intumescent flame retardant (IFR) technique has been considered as an alternative to halogen-based flame retardants for reducing the fire hazards of polymers, especially highly flammable polyolefins. However, the IFR technique possesses certain disadvantages, such as unsatisfactory flame retardant efficiency, high loading requirements, and toxic smoke release. In this study, zeolite imidazolate frameworks-8 (ZIF-8), a common type of metal−organic frameworks (MOFs), was incorporated into an IFR/polypropylene (IFR/PP) composite system as a synergist to further improve flame retardant efficiency and reduce the smoke emission. The results show that ZIF-8 and the IFR additives exhibit a strong synergistic effect between them for improvement of the formation and stability of the intumescent char layer, to prevent the intensive burning of PP. By adding only 2 wt % of ZIF-8, its limiting oxygen index value reached 31.2% and it obtained a UL-94 V-0 rating. From cone calorimeter test results, its peak heat release rate was further reduced by 44.1% and the total heat release at 700 s was reduced by 17.5% compared with the traditional IFR/PP system. The tendencies of fire spread and flashover were also reduced significantly. Furthermore, the addition of ZIF-8 could contribute to suppressing the smoke release as well as CO and CO 2 production from burning IFR/PP composites. Based on the analysis of carbonaceous residue, we propose that the presence of ZIF-8 in the IFR formula inhibits the size growth of the carbonaceous microdomain during combustion, which could help to form more compact char layers and ultimately improve the flame retardant efficiency. This study provides new insights for developing more efficient IFR systems for polyolefins and reducing their smoke emissions during combustion.

Enhancing anti‐meltdrop and smoke suppression properties of flame retardant poly(ethylene terephthalate) fabric by fiber‐blending method

“…43 The I D /I G value for FRV/POD/ FRPET (3:2:5) is the lowest between the ternary blended fibers, which is beneficial to form the more compact residual char. 44 The results are consistent with the characterization of the residual char morphology above.…”

Flame Retardant Coatings: Additives, Binders, and Fillers

“…To achieve the optimum flame retardant effect, thermal decomposition should occur close to the beginning of flame retardant degradation, with a subsequent release of flammable volatiles. Other than that, the shape and size of the fillers are also crucial factors to be considered [ 238 , 239 ]. Fillers’ particle size and the requirement for high addition levels to confer adequate flame retardancy are usually limiting their potential in intumescent flame retardant coatings, in terms of both processability and final physical properties [ 112 ].…”

Preparation of Graphene Quantum Dots Decorated Montmorillonite to Reinforce Fire Retardancy of Polystyrene

“…From the previous studies, it has been found that during the combustion process, volatile products are generated and released into the gas phase, and the combustion behaviors are mainly influenced by the production effect of the resulting char and gas inflation toward fractured char. Therefore, improving the quality and mass of chars is critical to reducing the flammability of polymers. – …”