Abstract:Multiferroic Ba1.6Sr1.4Co2Fe24O41 with a Z-type hexagonal structure was obtained through the proteic sol-gel process with a single-phase, combined with thermal treatment at 1200 °C for 2 h. XRD analysis revealed the formation of a single phase, with preferential orientation in the case of a sample in pellet form. Magnetometry measurements revealed a low coercive field characteristic of Z-type hexaferrite, plus an electrical resistivity of approximately 2 × 109 Ω.cm that was considerably higher than expected.
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.