Kinetics of extraction of the silicon, aluminum, and calcium of the basalt from the Daubaba deposit

Abstract

The article presents the results of the experimental studies of the kinetics of electric smelting of the basalt from the Daubaba deposit, the main components of which are 50.5% SiO 2 , 19.9% Al 2 O 3 , 9.3% CaO, 9.6% Fe 2 O 3 with the extraction of the silicon and aluminum into the ferroalloy, calcium into the calcium carbide. The effect of electric smelting time (from 10 to 60 minutes) and the amount of lime (from 0 to 30% from weight of basalt) on the degree of extraction of Si and Al into the alloy and Ca into CaC 2 was determined. The studies were carried out by the method of planning the experiments with the usage of roto-standard plans of second order (Box-Hunter plan) with exploring graphic optimization of technological parameters. The electric smelting was carried out in a graphite crucible. The mass of the furnace-charge in each experiment was 400 g. It was found that: extraction of Si, Al into the alloy, and Ca into the calcium carbide becomes noticeable in the first 10 minutes of the process; in the absence of lime, the maximum degree of extraction of the silicon, aluminum in the alloy and the calcium, respectively, contain 80.8%, 72.2% and 69% in 45 minutes; the presence of lime in the furnace-charge allows you to increase the degree of extraction of the calcium in the calcium carbide to 79.8%, however, at this time, the extraction of the silicon and aluminum decreases. To extract 77.1-86.8% of the silicon, 75-82% of the aluminum in the alloy and 75-79% of the calcium in the calcium carbide, the duration of the electric smelting should be 46-50 minutes and the amount of lime to 6.1% from weight of basalt.

Electrothermal processing of chrysotile-asbestos wastes with production of ferroalloy and extraction of magnesium into the gas phase

“…The optimal parameters were determined by combining the horizontal images in one figure. This method was described by us in articles [ [19], [20], [21], [22]].…”

Electrothermal production of ferroalloy from tripoli

“…Therefore, silica in tripoli is mainly in an amorphous state, a characteristic feature of which is an increased reactivity in comparison with the crystal form [4]. Using this property of amorphous silica, in contrast to the known methods of its application [ [5], [6], [7], [8], [9], [10]], it was proposed to use tripol as a silicon-containing raw material to produce a siliceous ferroalloy [11] for the smelting of which quartzite is used [ [12], [13], [14], [15]]. The article presents the results of studies to determine the optimal parameters for the electrothermal production of silicon ferroalloy from tripoli.…”