Investigation on Microbial Biodeterioration of the Stone Monuments in Yildiz Technical University—Yildiz Campus—Istanbul—Turkey

Özdemir, Ayşegül; Ergüven, Gökhan Önder; Adar, Elanur; Nuhoğlu, Yaşar

doi:10.1007/s00284-020-02171-4

Cited by 6 publications

(1 citation statement)

References 29 publications

(4 reference statements)

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Since biofilms are capable of periodically reestablishing themselves and are not easy to be washed away, they could cause cyclical biodeterioration processes [ 10 , 11 ]. Furthermore, biofilms accumulate water and allow microbial cells to survive adverse conditions [ 7 , 12 ].…”

Section: Introductionmentioning

confidence: 99%

On the Response to Aging of OPEFB/Acrylic Composites: A Fungal Degradation Perspective

et al. 2023

View full text Add to dashboard Cite

Biological agents and their metabolic activity produce significant changes over the microstructure and properties of composites reinforced with natural fibers. In the present investigation, oil palm empty fruit bunch (OPEFB) fiber-reinforced acrylic thermoplastic composites were elaborated at three processing temperatures and subjected to water immersion, Prohesion cycle, and continuous salt-fog aging testing. After exposition, microbiological identification was accomplished in terms of fungal colonization. The characterization was complemented by weight loss, mechanical, infrared, and thermogravimetric analysis, as well as scanning electron microscopy. As a result of aging, fungal colonization was observed exclusively after continuous salt fog treatment, particularly by different species of Aspergillus spp. genus. Furthermore, salt spray promoted filamentous fungi growth producing hydrolyzing enzymes capable of degrading the cell walls of OPEFB fibers. In parallel, these fibers swelled due to humidity, which accelerated fungal growth, increased stress, and caused micro-cracks on the surface of composites. This produced the fragility of the composites, increasing Young’s modulus, and decreasing both elongation at break and toughness. The infrared spectra showed changes in the intensity and appearance of bands associated with functional groups. Thermogravimetric results confirmed fungal action as the main cause of the deterioration.

show abstract