Investigation of the Efficiency of the Steel Tube Confinement Concrete Pillars Protection by Fire-Retardant Materials

Abstract

Currently, in Ukraine and abroad for the construction of high-rise buildings and structures using pipe-like structures. Wide application of pipe concrete columns is due to their high carrying capacity at relatively smaller overall dimensions due to the blocking of cracking in concrete by a steel clasp. The advantages of concrete columns should include more simplified conditions of technology of manufacturing and installation on their basis of bearing structures of floor covering.
 Piping constructions consist of steel shells and concrete core. Since the steel pipe mainly provides the bearing capacity of the concrete column, its failure or reduction of stiffness, which is characteristic of the fire under the influence of its thermal factors, leads to destruction. Investigation of fire resistance of concrete structures, which are not protected by flame retardant coatings, showed that a steel clasp during a fire after 15 minutes is heated to a critical temperature of 500 ° C.The use of flame retardant coatings is an effective method of fire protection of concrete constructions, which prevents the rapid heating of steel welds and provides a normalized fire resistance limit for such structures. In this work, studies were carried out on the effectiveness of fire protection of concrete columns with different types of fire-retardant materials - mineral wool slabs, special flame retardants and flame-retardant coatings. For fire protection mineral wool materials were used ROCKWOOL plates of the series "Conlit SL150". Mineral wool plates "Conlit SL 150" consist of fibers of rocks of a basalt group, they can withstand, without melting, temperature more than 1000 ° С. The silica-based adhesive "Conlit Glue" can withstand temperatures above 900 ° C, has good adhesion when bonding Conlit SL 150 mineral wool slabs with protective structures. From the second type of fire-retardant materials, the fire-proof composition "Naktresk" was chosen on the basis of gypsum. The coating is formed in the process due to hardening of the mixture on protected surfaces. The third type of flame retardant materials is the flame-retardant intumessent coating "Pyro-Safe Flammoplast SP-A2".It has been established that with the use of fire protection systems on the basis of mineral wool plates "Conlit SL150" and fire retardant "Nutresc", the fire resistance class of reinforced concrete columns increases from R 15 to R 180. The fire protection system on the basis of the painted paint "Pyro-Safe Flammoplast SP-A2" »Increases fire resistance from R 15 to R 75

Anti‐cracking performance test of thick steel structure fireproof coating under vibration fatigue load for critical health infrastructure

“…The fireproof mechanism of thick-coated steel structure fireproof coatings is mainly: (1) Use the incombustibility, low thermal conductivity and heat absorption of the component itself to delay the temperature rise of the steel; (2) use the large amount of halides contained in the material composition, Will decompose a large amount of hydrogen halide gas at high temperature, dilute oxygen and other combustible gases, inhibit combustion to delay the temperature rise of steel components. The paint has high bonding strength, excellent water resistance, good weather resistance, and light specific gravity and long fire resistance time [13]. Nguyen and others have studied the influence of fly ash and other raw materials on the thermal conductivity, and the thick steel structure fireproof coating prepared by the selected mix ratio has good high temperature resistance [14].…”

“…invented a water‐soluble paint with a weight ratio of fireproof paint: binder: water = 1:0.08:1.2. The paint has high bonding strength, excellent water resistance, good weather resistance, and light specific gravity and long fire resistance time [13]. Nguyen and others have studied the influence of fly ash and other raw materials on the thermal conductivity, and the thick steel structure fireproof coating prepared by the selected mix ratio has good high temperature resistance [14].…”