Investigating the Effect of CuO/NiO and CuO/CoO Relative Composition on the Reduction Time of (CuO)x-(NiO)(1-x) and (CuO)x-(Co3O4)(1-x) with Methane Gas as the Reducing Agent in the Synthesis of Nano-bimetallic Nix-Cu(1-x) and Cux-Co(1-x)

Abstract

In this paper, the reduction duration of (CuO)x-(NiO)(1-x) and (CuO)x-(Co3O4)(1-x) binary mixtures was studied using thermogravimetric method. The reduction reaction was performed using copper, nickel and cobalt oxides as metal precursors and methane gas as the reducing agent, under atmospheric pressure. The products as well as the raw materials were characterized and analyzed using X-Ray diffraction (XRD) and Energy Dispersive Spectroscopy (EDS). Initially, CoO, NiO and CuO were transformed to Co, Ni and Cu through reduction reactions with 23 Vol.% of methane at 830 °C. Results demonstrated that the reduction times of NiO, CoO and CuO NPs with CH4 at 830 °C were 14, 39 and 47 min, respectively. EDS and XRD analysis indicated that more than 97 % of copper, nickel and cobalt oxides were transformed to copper, nickel and cobalt NPs. The reaction time of (CuO)x-(NiO)(1-x) and (CuO)x-(Co3O4)(1-x) binary mixtures with methane was investigated to evaluate the effect of CuO (x=0, 0.4, 0.6, 1) relative composition. In addition, the reaction time of ternary mixture of (NiO)0.6-(CuO)0.2-(Co3O4)0.2 with methane gas was also studied.

One-Pot Combustion Synthesis of Lithium Nickel Cobalt Aluminium Oxide Cathode Material for Lithium-Ion Battery

“…3 displays the X-ray diffraction patterns of ternary metal oxide after the solution combustion process using flame gun. The samples were matched with the NiO sample from Ghanbarabadi and Khoshandam's research [34] and Joint Committee on Powder Diffraction Standards (JCPDS) card of NiO with number 44-1159. Furthermore, this result was confirmed by X-Ray Fluorescence characterization.…”