Interaction between thermoplastic starch and cellulose in poly (butylene adipate-co-terephthalate) composites with cellulosic fillers

In this paper, using Styphnolobium japonicum, Cryptomeria fortunei and Pinus yunnanensis as raw materials, cellulose (CE) was first extracted by chemical method (CM1) and biological enzymatic method 2 (BM2), and then further prepared into nanocellulose fiber (CNF) by biological enzymatic method 1(CPM (CPM stands for cellulase and pectinase)). The CE and CNF were characterized by FTIR, XRD, SEM, DSC and TG. The results showed that the CNF prepared by CM1-CPM was cellulose type II, CNF prepared by BM2-CPM was cellulose type I. The best crystallinity of the CNF prepared by CM1-CPM reached 74.1% ( C. fortunei CNF), the best yield was 24.0% ( S. japonicum CNF) and the minimum average diameter was 62.6 nm ( C. fortunei CNF). However, the best crystallinity of CNF prepared by BM2-CPM reached 80.1% ( C. fortunei CNF), the best yield was 27.4% ( C. fortunei CNF), and the minimum average diameter was 31.6 nm ( C. fortunei CNF). And also, the thermal degradation analysis of the CNF prepared from the three raw materials revealed that the CNF prepared by BM2-CPM had better thermal degradability. Finally, the thermal stability analysis of the C. fortunei CNF was carried out, and it was found that the residual mass of CNF prepared by BM2-CPM was 48%, while the residual mass of C. fortunei CNF prepared by BM1-CPM was 22%, which showed the C. fortunei CNF prepared by BM2-CPM had better thermal stability. Therefore, the properties of nanocellulose prepared by BM2-CPM are optimal.

Section: Xrd Analysis For Cellulose and Nanocellulosementioning

confidence: 99%

Section: Introductionmentioning

confidence: 99%

See 1 more Smart Citation

Preparation and characterization of nanocellulose fiber (CNF) by biological enzymatic method

Wang

Song

Cui³

et al. 2023

“…Cellulose is also known as a carbohydrate polymer that could be used as a compatibilizer for polyester materials, namely thermoplastic starch. 49 This is because there is growing interest in manufacturing biocomposite materials made of natural cellulose in a thermoplastic matrix. 50…”

Section: Source Of Nanocellulose From Natural Fibermentioning

confidence: 99%

A review of nanocellulose modification and compatibility barrier for various applications

James,

Rahman,

Mohamad Said

et al. 2023

Nanocellulose is increasingly important due to its abundance and sustainability sources, outstanding physicochemical properties, low density, high specific surface area, and easily modified surface chemistry. Nanocellulose is obtained from various sources, such as plants, algae, and bacteria, with plant-derived nanocellulose being the most common. Their presence significantly benefits many applications, especially in developing advanced materials for high end-use. Despite these benefits, the intrinsic hydrophilic behavior complicates dispersion in hydrophobic polymer matrices due to aggregation issues that result in deterioration properties. Nanocellulose modification and surface tuning are identified as fundamental approaches for improving the compatibility of the interfacial interaction between nanocellulose and polymer matrix to impart new functionalities to novel advanced materials. This article offers insight into nanocellulose by highlighting various lignocellulosic biomass sources and their chemical constituents. Three categories of nanocellulose are discussed in this review, including cellulose nanocrystals, cellulose nanofibrils, and bacterial nanocellulose. This article also featured several methods for promoting surface modification of nanocellulose to overcome the compatibility barrier between nanocellulose and polymer matrix to achieve a balanced hydrophilic-hydrophobic behavior. A few recent and emerging applications of nanocellulose-based composites are also presented in this review.

“…70 Residues from pyrolysis at 700°C are related to non-volatile materials and materials the effect of the char formed by degraded starch. 71 So the increase in the percentage of residues is related to the incorporation of more solids in relation to the dry mass of starch, causing a reduction in the amount of water in the sample.…”

Section: Morphological Evaluation Of Filmsmentioning

confidence: 99%

Development and evaluation of biodegradable starch-based films containing cellulose nanocrystals/titanium dioxide nanoparticles as an alternative for food packaging

Picolotto,

Rossa Beltrami,

Dallé

et al. 2023

Biodegradable starch-based films are an environmentally friendly solution to reduce the use of petroleum-derived polymers. Thus, this work aims to obtain corn starch films by incorporating 5% w/w of cellulose nanocrystals (CNC), different concentrations of titanium dioxide nanoparticles (TiO2) (0, 0.25, 0.5, 1, and 2% w/w), and 40% w/w of glycerol and sorbitol (plasticizers), in a 1:1 ratio. The films showed a high potential for UV-light barrier, with an increase of 307% incorporating only 2 wt% of TiO2 in relation to the film without incorporation of TiO2. The use of TiO2 increased the white pigmentation capacity of the samples and decreased the lower water solubility – a reduction of approximately 28% using 0.5 wt% TiO2 compared to the CNC control sample was observed. The incorporation of TiO2 nanoparticles increased the tensile strength by adding 1 wt% of TiO2 nanoparticles with 34% increase in the tensile strength of the film without incorporation of TiO2. The thermal stability of the films with 1 wt% TiO2 and 5 wt% CNC increased by 85°C. Thus, the addition of CNC and TiO2 enabled an improvement in the physical/thermal/chemical properties of the films, making them possible alternatives for use in food packaging.