Influence of the interaction of components in a transient layer of oxide film—glass substrate on properties of the composite material

SiO2 barrier layer influence on the glass composites with oxide nano films laser ablation destruction

“…Drawing speed -3.8 mm/s It has been derived that the threshold energy density value increases with higher reflectivity coefficient values, which is explained by the ratio of the laser radiation reflected energy at the film surface increasing. The reflectivity coefficient decreasing in the double-layer films is bound to the film refractive index lowering due to the SiO 2 barrier layer as well as in [12].…”

“…This dependence is due to the sol particles packing density in a layer increases with the drawing speed from the sol particles diameter decreasing. Its increasing, probably, is connected with the influence of the light dispersion which is more, than more the film thickness for the film refractive index dependence on its thickness [12].…”

“…The heat treatment in the microwave oventhe furnace was made within 30 minutes. The thickness, refractive index, film reflectivity have been measured by the Horiba Jobin Yvon type spectra ellipsometer as in [12] and the samples light transmittance by a FSD-8 type micro spectrometer (NCFO RAS).…”

“…Such the difference of these properties measurements result can be connected with various structure and composition of the complexes which are formed in these films [3,4,12].…”

Взаимосвязь Оптической И Механической Прочности Композитов С Покрытиями, Полученными Из Золей

“…Следует отметить, что стеклянный композит, изученный в рамках настоящей работы, представляет собой достаточно твердую и тугоплавкую стеклянную подложку, поверх которой нанесено пористое и потому менее твердое покрытие. С другой стороны, покрытия, полученные из растворов-золей и характеризующиеся весьма обширной переходной зоной " подложка−покрытие", считаются " твердыми" покрытиями [6][7][8]. Возможно, именно проникновением компонентов подложки в промежуточный слой " покрытие−подложка" и компонентов покрытия в этот же слой объясняется упрочняющий эффект зольгель покрытий на стекле.…”