Influence of Processing Type in the Morphology of Membranes Obtained from PA6/MMT Nanocomposites

Ferreira, Rodholfo da Silva Barbosa; Pereira, Caio Henrique do Ó; Paz, Renê Anísio da; Leite, Amanda Melissa Damião; Araújo, Edcleide Maria; Lira, Hélio Lucena

doi:10.1155/2014/659148

Cited by 7 publications

(9 citation statements)

References 15 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…According to Figure 3(b2,c2), the addition of clay led to a decrease in the filtering skin attached to the membrane porous support, increasing the porosity of the support as compared to the pure PES membranes. This phenomenon was also observed by the authors in [18][19][20]. The increase in porosity The addition of clay, which is hydrophilic, gives the membrane surface this characteristic [15,16].…”

Section: Effect Of Clay On Membrane Hydrophilicitysupporting

confidence: 72%

Treatment of Effluents from the Textile Industry through Polyethersulfone Membranes

Ferreira

Salviano

Oliveira

et al. 2019

Water

View full text Add to dashboard Cite

Membranes have been widely used in the treatment of industrial effluents. However, there are still some limitations in the separation and permeability with respect to these effluents. Therefore, this study investigated the addition of 1% and 5% of an inorganic filler (clay) in polyethersulfone polymer membranes. By contact angle analysis, it was observed that the clay influenced the hydrophilicity of the membrane. The presence of the clay had an important role in the morphology of the membrane, modifying and favoring a greater quantity of pores and macropores for the porous support. For the tensile test, it was seen that the high clay content decreased the membranes properties. The flow tests, having a flow stabilized around 300 L/h·m 2 for membranes containing clay, evidenced the efficiency of the membrane for the treatment of indigo blue, representing a 200% increase in relation to polyethersulfone membrane. The membrane containing 1% of clay presented the highest level of rejection to the effluent, around 94.0%. Thus, it was evident that the addition of montmorillonite clay modified the membrane structure contributing to a higher selectivity and permeability.

show abstract

Section: Effect Of Clay On Membrane Hydrophilicitysupporting

confidence: 72%

Treatment of Effluents from the Textile Industry through Polyethersulfone Membranes

Ferreira

Salviano

Oliveira

et al. 2019

Water

View full text Add to dashboard Cite

show abstract

“…21.8° of the crystalline plan (001), which can be attributed to phase γ (gamma) of PA6 36,37 . The addition of 10% w/w of CaCl 2 in the solution of membrane preparation did not cause significant changes with regard to the crystalline behavior and the main crystalline phase is α, as illustrated by the X-ray diffraction curve of pure PA6 membranes and their hybrids.…”

Section: Water Permeability and Oil Retentionmentioning

confidence: 99%

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

et al. 2017

Self Cite

View full text Add to dashboard Cite

In this work, it was prepared hybrid membranes of polyamide6 (PA6) with montmorillonite (MMT) and porogenic agent (CaCl 2 ). The hybrid membranes with CaCl 2 were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), porosimetry by mercury intrusion (PMI), flux measurements and rejection. By means of X-ray diffraction, it was revealed that the hybrid membranes with CaCl 2 have an exfoliated and/or partially exfoliated structure. For FTIR and DSC of hybrid membranes with CaCl 2 , it was found that the spectra and the crystalline melting temperature remained virtually unchanged compared to PA6 membrane. From the SEM images, it was observed that the addition of the MMT and the CaCl 2 in the membrane of PA6 caused an increase in the amount of pores the surface and cross section of these membranes. By PMI, it was observed that the presence of MMT and CaCl 2 in the membrane caused an increase in the average diameters of pores. The water-oil separation tests, indicated a significant reduction of oil in the permeate, allowing treatment of wastewater contaminated with oil.

show abstract

“…É possível observar ainda nas membranas híbridas obtidas, a ausência do pico característico da argila que se posiciona entre 5-7°, indicando uma possível esfoliação e/ou esfoliação parcial. Entretanto, para a membrana de PA6 com 1% de argila, aparece um ombro no intervalo entre 2,5 a 4,0º, o que se deve a uma provável intercalação parcial das lamelas da argila [25,27].…”

Section: Figuraunclassified

“…Analisando a PA6 pura e seus híbridos, foi possível observar que a fase cristalina predominante é a alfa [24][25][26]29]. Além disso, foi constatada nas membranas com 3% e 5% de argila, a presença de um pico em aproximadamente 27°, referente ao elemento quartzo da argila.…”

Section: Figuraunclassified

“…As cargas minerais do tipo bentonita são facilmente encontradas na região da Paraíba. Elas vêm sendo utilizadas em nanocompósitos e apresentando resultados bastante promissores para aplicações em membranas híbridas; dessa forma, o estudo destas é interessante não só do ponto de vista tecnológico, mas também um incentivo para as indústrias locais [23][24][25][26][27].…”

Section: Introductionunclassified

See 1 more Smart Citation

Membranas microporosas híbridas assimétricas: influência da argila na morfologia das membranas

Medeiros¹,

Araújo²,

Lira³

et al. 2017

Matéria (Rio J.)

Self Cite

View full text Add to dashboard Cite

RESUMO Neste trabalho, foram obtidas membranas híbridas de poliamida6 (PA6) com 1%, 3% e 5% em peso de argila na forma de filmes finos por meio da técnica de inversão de fases. As membranas híbridas foram caracterizadas por difração de raios-X (XRD), espectroscopia na região do infravermelho com transformada de Fourier (FTIR), calorimetria exploratória diferencial (DSC), microscopia eletrônica de varredura (SEM), porosimetria por intrusão de mercúrio (MIP) e ângulo de contato. Por meio do XRD, foi possível perceber que as membranas híbridas sugerem uma estrutura esfoliada e/ou parcialmente esfoliada. Os espectros de FTIR das membranas híbridas permaneceram inalterados, exceto pelo aumento na intensidade dos picos em 800, 1033 e 1095 cm−1 provavelmente referente à camada octaédrica e a vibração do estiramento do grupo Si- O-Si da argila. Por DSC foi observado que praticamente não houve alteração da temperatura de fusão cristalina das membranas híbridas em relação à membrana de PA6 pura. A partir das fotomicrografias obtidas por SEM, foi ilustrada a obtenção de membranas microporosas assimétricas com a formação de uma pele filtrante e um suporte poroso ao longo da seção transversal. Além disso, a adição da argila provocou um aumento na quantidade e distribuição uniforme dos poros existentes na superfície e seção transversal destas membranas. Por MIP, observou-se que a presença da argila nas membranas ocasionou um aumento nos diâmetros médio dos poros. Por meio do ângulo de contato, verificou-se que as membranas híbridas apresentaram maiores ângulos de contato para a água destilada quando comparadas aos ângulos obtidos com o óleo sintético. As membranas híbridas obtidas apresentaram uma morfologia com porosidade adequada para aplicação em processos de microfiltração.

show abstract

Influence of Processing Type in the Morphology of Membranes Obtained from PA6/MMT Nanocomposites

Cited by 7 publications

References 15 publications

Treatment of Effluents from the Textile Industry through Polyethersulfone Membranes

Treatment of Effluents from the Textile Industry through Polyethersulfone Membranes

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

Membranas microporosas híbridas assimétricas: influência da argila na morfologia das membranas

Contact Info

Product

Resources

About