Influence of heat treatment and aging on microstructure and mechanical properties of Mg‐1.8Zn‐0.7Si‐0.4Ca alloy

Abstract

In order to optimize the aging treatment of Mg‐1.8Zn‐0.7Si‐0.4Ca alloy, different times and temperatures of solid solution and age hardening were applied to the alloy specimens. Microstructures and mechanical properties of the specimens were investigated using the optical microscopy, field emission scanning electron microscopy equipped with an energy dispersive x‐ray spectrometer, x‐ray diffraction, hardness, and shear punch tests. The lowest hardness and strength were achieved by solution treating of the alloy at 500 °C for 8 h, presenting the optimal condition for solution treatment of the alloy. The microstructural examinations revealed three different precipitates consisting of CaMgSi, Ca2Mg6Zn3, and Mg2Si in the solid solution specimens. It was found that the highest peak hardness and strength are obtained by aging the alloy at 150 °C for 16 h. This condition was confirmed by differential scanning calorimetry (DSC) tests performed on the solid solution and aged specimens.

Effect of Artificial Aging Treatment on the Mechanical Properties and Regulation of Precipitated Phase Particles of High-Pressure Die-Cast Thin-Wall AlSi10MnMg Longitudinal Carrier

“…This strategy facilitates the alloy in achieving enhanced mechanical properties within a relatively shorter duration, thereby augmenting the efficiency of the heat treatment process. When juxtaposed with conventional single-aging treatments, double-aging considerably bolsters the alloy’s tensile strength, elongation, and hardness [ 31 ].…”