Influence of Fineness Levels and Dosages of Light-Burned Dolomite on Portland Cement Performance

Abstract

The paper aims to understand the effect of light-burned dolomite powders (LBD) on ordinary Portland cement (OPC) and evaluate the influence of LBD dosages and fineness levels on the mechanical properties and hydration properties of OPC. The LBD/OPC pastes were prepared by OPC blended with LBD at various replacement dosages and fineness levels. The mechanical properties were studied by flexural and compressive strength tests, while the hydration properties were investigated by X-ray diffraction (XRD), thermogravimetric analysis (TG), differential scanning calorimetry (DSC), and reaction degree of LBD. Experiment results indicated that the flexural and compressive strength of LBD/OPC samples were higher than reference sample at all ages. The fineness levels of LBD was C (C-LBD) with 0.5–1.5 wt% dosages, and the fineness levels of LBD was B (B-LBD) with 1.5–2.5 wt% dosages can significantly improve the strength of cement-based materials. The main mineral components of LBD are MgO and CaCO3, of which MgO could react with water to form Mg(OH)2 quickly, and CaCO3 could hydrate with C3A to from hydrated calcium carboaluminate (C3A·CaCO3·11H2O), which prevents the conversion of AFt to AFm.

Influence of Mechanical Grinding on Particle Characteristics of Coal Gasification Slag

“…Previous studies have shown that the particle size gradation of Portland cement has a significant effect on its mechanical properties [ 40 , 41 , 42 ]. Among them, the number of particles in the range of 0–3 μm and 3–24 μm has a significant impact on the mechanical properties of the cured samples for 1 d and 28 d, respectively.…”