Influence of Different Types of Initial Bimodal Grain Structures on Indicators of Superplasticity

Abstract

The peculiarities of the superplasticity effect of the aluminium Al-Zn-Mg-Cu-Zr system alloy with two types of initial grain structure are considered. For the first type of structure, the large grains are predominant, and submicrocrystalline grains take up less volume. Another type of grain microstructure is that of large grains, rounded by small submicrocrystalline grains, which occupy a significantly larger relative volume. Samples with both types of microstructure exhibit superplastic properties, however, the range of flow stresses and strain rates in which the alloy samples are superplastic is much wider for a microstructure where submicrocrystalline grains predominate. For both types of microstructure, deformation processes are mainly localized in those volumes of samples where submicrocrystalline grains were concentrated. However, large grains change their shape during superplastic deformation. The reason for this may be the manifestation of the hydrodynamic flow during the process of deformation.

Surface Morphology and Properties of the Surface Layer of AA6111 Aluminium Alloy Treated by a Pulsed Beam of Relativistic Electrons

“…Максимальне видовження до зруйнування при кімнатних температурах складає 21%. При високих гомологічних температурах, незважаючи на досить крупний розмір зерен, стоп демонструє надпластичну поведінку [15]. При температурі Т = 793 К і швидкості істинної деформації ксимальне поглинання енергії ІЕП доводиться на підповерхневу область, відбувається мікровибух поверхні, що супроводжується ударно-пластичною хвилею в напрямку мішені та викидом матеріялу в сторону дії пучка [2][3][4][5][6][7][8][9].…”