Indentation Measurement of CuZnAl Dual Phase Shape Memory Alloy

Abstract

The aim of this work is indentation study of local mechanical properties of Cu-22Zn-4.6Al alloy, which has significant shape memory effect after quenching from dual α + β phase region. The study was carried out on the samples with thermoelastic and non-thermoelastic martensite in the structure, which were obtained by quenching from various temperatures. A different behavior concerning mechanical properties measurements of α phase and β phase transformed to martensite after quenching from various temperatures was found out. It was observed almost no change of mechanical properties of α phase, whereas indentation hardness HIT and indentation modulus EIT raised with increasing quenching temperature. Also some serious differences were observed at indentation test of thermoelastic and non-thermoelastic martensite.