The effect of several variables such as molar ratio P 2 O 5 /B 2 O 3 (X), temperature and heating cycle on the strength of chemically bonded SiC materials for grinding wheels fabrication was studied. It was shown that the highest compressive strength (52.4 MPa) could be obtained using an optimal molar ratio X = 4.5 and a multiple step heating cycle up to a sintering temperature of 800 o C. DTA, XRD, SEM and dilatometrical analysis were performed to follow the different stages of the structural development.Keywords: phosphate bonding, strength, grinding tools, SiC, chemical bonding.
Sinterizacion de nuevos materiales compuestos de sic aglomerados con fosfatos para la fabricacion de muelas abrasivasSe estudia el efecto de diferentes variables tales como la razón molar P 2 O 5 /B 2 O 3 (X), temperatura y ciclo de calentamieno sobre la resistencia de materiales de SiC aglomerados quimicamente para la fabricación de muelas arasivas. Se ha comprobado que la más alta resistencia a la compresión (52,4MPa) pueda obtenerse usando una razón molar òptima x= 4,5 y un ciclo de calentamiento en múltiples etapas hasta la temperatura de 800º C. Estudios mediante ATD, DRX, MEB y análisis dilatométricos fueron llevados a cabo para seguir las diferentes etapas del desarrollo microestructura.
Palabras clave: Aglomeración química, resistencia mecánica, muelas abrasivas de SiC