Improved Hemolytic Performance of Blood Pump with Fluorine-Doped Hydrogenated Amorphous Carbon Coating

Abstract

<p class="MsoNormal"> <span lang="EN-US">Fluorine-doped hydrogenated amorphous carbon (a-C:H:F) film was deposited on a flow-straightener, impeller and diffuser surface (SUS 304) of an enclosed-impeller type flow blood pump using the ionization deposition method with a source gas of C₆F₅H. The surface characteristics of the a-C:H:F film were examined using atomic force microscopy, X-ray photoelectron spectroscopy, and measurements of surface roughness, friction and surface potential. The a-C:H:F film tends to increase surface roughness and the negative surface charge. In addition, the surface energy and friction decrease with fluorine dopant in the a-C:H film. To estimate the hemolytic performance of a blood pump with the a-C:H:F film coating, the amount of hemolysis was measured using a mock circulatory system (<i>in vitro</i> test) with 500 mL of pig blood containing sodium citrate. <i>In vitro</i> test was conducted for 180 min with the blood flow and pump head maintained at 5 L/min and 100 mmHg, respectively. The a-C:H:F film coating reduced the amount of hemolysis and improved the hemolytic performance. Decreasing the surface energy and negative surface charge of the a-C:H:F film contributes to the improvement of the hemolytic performance. The a-C:H:F film coating is thus expected to be utilized in medical technology as a surface coating technology for artificial heart blood pumps.</span> </p