Green inhibitor of carbon steel corrosion in 1 M hydrochloric acid:Eruca sativaseed extract (experimental and theoretical studies)

Abstract

The adsorption activity and inhibition effect of Eruca sativa seed extract as a green inhibitor for the dissolution of carbon steel in 1 M hydrochloric acid solution were investigated.

WITHDRAWN: Anticorrosive concert of expired drug acts as novel and potent inhibitor for deterioration of Low carbon steel in acidic Environment

“…This corrosion should be avoided or controlled otherwise it destroy the unique properties of low carbon steel. In India the cost of scale wastes from the industries is 26.1 billion USD, it is equal to 2.4 % of total GDP [1--9], the different types of heterocyclic organic compounds containing N, O, S and P molecules has been noted as corrosion inhibitors, The speci c was adsorbed on the low carbon steel surface and removed the metal's corrosion active sites, [10][11][12][13][14][15][16][17][18][19][20][21][22]. The following three major factors in uence inhibitor adsorption: metal type and nature, chemical structure of the inhibitor molecule, and medium of the metal present.…”

Cysteine as an Eco-Friendly Anticorrosion Inhibitor for Mild Steel in Various Acidic Solutions: Electrochemical, Adsorption, Surface Analysis, and Quantum Chemical Calculations

“…and MSL. Based on the studies from several publications, the electronegativity of Fe is 4.28 V/mol, and its stiffness is 0 V/mol. − The local reactivity of a molecule was finished using Fukui function accounting as well. For electrophilic and nucleophilic assaults by inhibitor molecules, Fukui+ and Fukui, respectively, are the favored targets.…”

Co3O4 quantum dot decorated polypyrrole nanocomposites as a flexible, conducting, anticorrosive and antibacterial agent: sustainable experimental and theoretical approach

“…MS sheets were polished mechanically using sandpaper (150 to 800 grade). 22,23 The American standard test method (ASTM-D-2688) was adopted to estimate the corrosion rate (CR). 24 The MS specimens aer mechanical polishing were exposed to 0.1 M HCl solution for 24 h. Aer 24 h, the MS specimens were washed initially with tap water, dried, and then wiped with acetone.…”