Fundamental investigation of the degradation laws of aluminide coatings during high‐temperature oxidation

Abstract

During high-temperature oxidation, the aluminide coating degrades by two mechanisms, one is the oxidation of the outer surface, and the other is Al diffusion into the substrate. The relevant laws are investigated for coatings on Co-base superalloys oxidised in air at high temperatures. The driving force mainly comes from the oxidation reaction for the outer degradation layer, and the chemical potential for the inner degradation layer. By an approximation approach, it can be concluded that the life of the outward-diffusion coating is roughly directly proportional to the second power of the main-phase thickness of the coating.Wa Èhrend Hochtemperaturoxidation kann die Aluminidbeschichtung durch zwei Mechanismen gescha Èdigt werden; der eine ist die Oxidation der a Èuûeren Oberfla Èche und der andere ist die Al-Diffusion in das Grundmaterial. Fu Èr Beschichtungen auf Co-basierenden Superlegierungen, die in Luft bei hohen Temperaturen oxidiert wurden, sind die relevanten Gesetze untersucht worden. Die Triebkraft kommt im wesentlichen von der Oxidationsreaktion fu Èr die gescha Èdigte a Èuûere Schicht und vom chemischen Potential fu Èr die gescha Èdigte innere Schicht. Mit Hilfe eines Na Èherungsansatzes kann gefolgert werden, dass die Lebensdauer der nach auûen diffundierenden Beschichtung in etwa direkt proportional der zweiten Potenz der Dicke der Hauptphase der Beschichtung ist. Materials and Corrosion 54, 93±96 (2003) High-temperature oxidation of aluminide coatings 93