Abstract

The formation enthalpy of the BLi (B 48 Li 52 ) intermetallic phase was measured with the use of the water reaction and the direct reaction calorimetric method. The phase was prepared of weighed amounts of B and Li in a glove-box filled with high purity argon. The BLi phase was confirmed with using the X-ray diffraction investigations. The experiments were carried out with the use of a water reaction calorimeter (water reaction calorimetric technique) at 25• C (298 K) in air, as well as a direct reaction calorimeter at 752• C in high purity argon. The formation enthalpy value obtained for the BLi phase in the case of the water reaction calorimetric method equaled -30.3±2.2 kJ/mole of atoms and in the case of the direct synthesis technique -29.4±2.0 kJ/mole of atoms.Keywords: Boron-lithium system, calorimetry, thermochemistry, hydrogen storage Entalpia tworzenia fazy międzymetalicznej BLi (B 48 Li 52 ) została zmierzona przy użyciu metody rozpuszczania w wodzie oraz metody bezpośredniej reakcji. Faza była wytworzona w komorze manipulacyjnej w atmosferze oczyszczonego argonu z odpowiednich naważek B oraz Li. Eksperymenty zostały przeprowadzone przy użyciu kalorymetru wodnego (technika kalorymetryczna pozwalająca na pomiar reakcji z wodą) w 25• C (298 K) w powietrzu, a także przy użyciu metody bezpośredniej reakcji w 752• C w atmosferze argonu o wysokiej czystości. Uzyskana wartość entalpii tworzenia fazy BLi w przypadku kalorymetrycznej metody reakcji z wodą wynosiła -30,3±2,2 kJ/mol atomów a w przypadku metody bezpośredniej reakcji: -29,4±2,0 kJ/mol atomów.

The B-Li System. Calorimetric and Theoretical Studies / Układ B-Li. Badania Kalorymetryczne I Teoretyczne

“…The samples were prepared in the MBraun glove-box filled with high purity argon, similarly to our previous calorimetric measurements [30][31]. The alloys were prepared by way of melting the metals in Mo crucibles with a cover, which were placed in Ni crucibles and sealed with a Ni stopper by means of a hydraulic press.…”

“…This paper is a continuation of our study on the heat of formation of the intermediate phases of the B-Li system [30][31] 13 , respectively, as well as the phonon results will allow us to understand the stability dependence on the temperature for these phases, which, to the best of our knowledge, were herein optimized for the first time.…”