Fenestrated aortic endograft branching with Gore VBX poses failure risk from delayed-onset branch kinking

Kuwayama, David P.

doi:10.1016/j.jvscit.2018.08.011

Cited by 11 publications

(8 citation statements)

References 8 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…8,9 Initial experience with this BSG has been described in combined fenestrated/branched EVAR (f/bEVAR) and chimney EVAR/fEVAR (chEVAR/fEVAR) cohorts with diverging results, which do not allow a discrimination of VBX stent-graft performance under different technical requirements. [8][9][10][11][12] So far, the stent has not been extensively assessed in a solely TAAA cohort. The aim of this study is to evaluate the VBX as a bridging device in bEVAR for TAAAs.…”

Section: Introductionmentioning

confidence: 99%

See 1 more Smart Citation

Performance of the Gore VBX Balloon Expandable Endoprosthesis as Bridging Stent-Graft in Branched Endovascular Aortic Repair for Thoracoabdominal Aneurysms

et al. 2021

View full text Add to dashboard Cite

Purpose Bridging stent stability is crucial for efficacy and safety of branched aortic endovascular repair (bEVAR) of thoracoabdominal aortic aneurysms (TAAAs). In this study, we assess the performance of the new Viabahn Balloon-Expandable endoprosthesis (VBX) in bEVAR. Based on our learning curve we give recommendations for a safe and effective use of the device. Materials and Methods We prospectively collected the data of patients with TAAAs undergoing bEVAR between December 2017 and December 2019. All patients with implantation of at least 1 VBX stent-graft as bridging stent were included in our single-center analysis. Demographic, comorbidity, and computed tomography angiography (CTA) data of 112 patients were retrospectively evaluated. Primary endpoint was a composite of branch-related technical success and freedom from target vessel instability. Secondary endpoints were clinical and ongoing clinical success. Results Primary endpoint: technical success was achieved in all patients (100%) with a freedom from target vessel instability of 96.3% after a median follow-up of 18 months. Overall mortality was 13.4% (n=15) and 13 patients underwent secondary interventions, 12 of them are still alive and 1 suffered from aneurysm sac expansion, consequently an ongoing clinical success of 75.9% was reached. After modification of the implantation technique during the course of the study by selecting longer stent lengths after accurate estimation of vessel curvature and expected adaptation of the flexible endoskeleton to the specific anatomical conditions, no type Ic endoleaks were observed in the last 70 cases. Conclusions The VBX stent-graft can be safely used as bridging stent for branched thoracoabdominal repair. However, learning curve should be considered to avoid type Ic endoleak and edge stenosis. Based on this experience longer landing zones and 2-step deployment of VBX are useful for successful bridging also of challenging target vessels.

show abstract

Section: Introductionmentioning

confidence: 99%

Section: Introductionmentioning

confidence: 99%

Performance of the Gore VBX Balloon Expandable Endoprosthesis as Bridging Stent-Graft in Branched Endovascular Aortic Repair for Thoracoabdominal Aneurysms

et al. 2021

View full text Add to dashboard Cite

show abstract

“…However, the report lacked adequate imaging, limiting the conclusions that can be drawn from this isolated case. 13…”

Section: Discussionmentioning

confidence: 99%

Comparison of the Biomechanical Properties of the Advanta V12/iCast and Viabahn Stent-Grafts as Bridging Devices in Fenestrated Endografts: An In Vitro Study

et al. 2020

View full text Add to dashboard Cite

Purpose: To compare experimentally the biomechanical properties of the Viabahn Balloon-Expandable Stent Graft (VBX) with the widely used Advanta V12/iCast in the role of bridging stent-grafts for fenestrated endovascular aortic repair. Materials and Methods: Test sheets made of polyester having 2 rows of 5 fenestrations in 6-mm and 8-mm diameters were used to simulate a commercially made fenestrated aortic endograft. In total, 40 stent-grafts measuring 6×39 mm and 8×39 mm (10 of each size for each stent-graft) were implanted in fenestration sheets immersed in a 37°C water bath. After flaring, all stent-grafts were evaluated using microscopy and radiography. Biomechanical evaluation included pullout and the shear stress force testing; results are reported in Newtons (N) as the median (minimum–maximum). Results: After flaring, no damage or fracture to the stent-graft structures were detected. Pullout forces for the 6-mm stent-grafts were 27.1 N (20.0–28.9) for the VBX and 16.6 N (14.7–19.2) for the Advanta (p=0.008). Pullout forces for the 8-mm stent-grafts were 20.1 N (14.8–21.5) for the VBX and 15.8 N (12.4–17.5) for the Advanta (p=0.095). The shear stress forces necessary to dislocate the device at 150% stent diameter displacement was 12.5 N (VBX) vs 14.7 N (Advanta) for the 6-mm devices and 23.3 N (VBX) vs 20.2 N (Advanta) for the 8-mm stents (p>0.99 and p=0.222, respectively). Conclusion: In vitro tests simulating external pull and shear forces on bridging stent-grafts implanted in fenestrations showed that the VBX had resistance to dislocation equivalent to a well-known control device.

show abstract

“…The stent is fully encapsulated in the fluoropolymer and the inner surface is covered with a stable, covalently bound bioactive heparin of porcine origin. 2,11,15…”

Section: Methodsmentioning

confidence: 99%

“…The stent is fully encapsulated in the fluoropolymer and the inner surface is covered with a stable, covalently bound bioactive heparin of porcine origin. 2,11,15 The Advanta V12 (Getinge) endoprosthesis is a balloon-expandable stent-graft. It is characterized by a stainless-steel stent encapsulated in an ultrathin PTFE fabric.…”

Section: Description Of the Stent-graftsmentioning

confidence: 99%

Fatigue Resistance of the Advanta V12/iCast and Viabahn Balloon-Expandable Stent-Graft as Bridging Stents in Experimental Fenestrated Endografting

et al. 2021

View full text Add to dashboard Cite

Purpose: Bridging stents undergo millions of cycles during respiratory movements of the kidneys throughout the patient’s life. Thus, understanding the response of fabric and endoskeleton of the stent to cyclic loading over the time is crucial. In this study, we compare the fatigue resistance of the Viabahn Balloon-Expandable stent-graft (VBX) with the widely used Advanta V12/iCast under prolonged stress induction. Materials and Methods: A polyester test sheet with 10 fenestrations was used simulating a fenestrated endograft. Five 6×59 mm VBX stent-grafts and five 6×58 mm Advanta stent-grafts were implanted into 6×6 mm fenestrations. The stents were flared with a 10×20 mm PTA (percutaneous transluminal angioplasty) catheter and connected with a fatigue stress machine. All stent-grafts were evaluated by microscopy and radiography at baseline and after regular intervals until 50,000,000 cycles were applied, simulating a life span of approximately 75 months. Freedom from fracture (FF), freedom from initial polytertafluoroethylene (PTFE) changes (FIC), and from PTFE breakpoint (FBP, all-layer defect) were calculated. Results: Digital radiographic images did not show any stent fracture in both groups after 50,000,000 cycles. The VBX stent-graft was free from any all-layer defects at the conclusion of 50,000,00 cycles resulting in a significant higher FBP compared with Advanta V12 (50,000,000 vs 33,400,000; p<0.01). All-layer defects were observed only in the Advanta group. Two of 5 Advanta stents showed early penetration of the nitinol ring causing a defect of PTFE. Regarding FIC, there was no significant difference between the stents (3,400,000 in VBX vs 3,200,000 in Advanta). Conclusions: In fatigue tests simulating respiration movements, VBX and Advanta V12 performed equally well in terms of fracture resistance and freedom from initial PTFE changes. VBX maintained freedom from PTFE breakpoint throughout the full 50,000,000 cycles. All-layers defects were detected only in Advanta and were mainly caused by penetration of the nitinol ring through the PTFE.

show abstract

Fenestrated aortic endograft branching with Gore VBX poses failure risk from delayed-onset branch kinking

Cited by 11 publications

References 8 publications

Performance of the Gore VBX Balloon Expandable Endoprosthesis as Bridging Stent-Graft in Branched Endovascular Aortic Repair for Thoracoabdominal Aneurysms

Performance of the Gore VBX Balloon Expandable Endoprosthesis as Bridging Stent-Graft in Branched Endovascular Aortic Repair for Thoracoabdominal Aneurysms

Comparison of the Biomechanical Properties of the Advanta V12/iCast and Viabahn Stent-Grafts as Bridging Devices in Fenestrated Endografts: An In Vitro Study

Fatigue Resistance of the Advanta V12/iCast and Viabahn Balloon-Expandable Stent-Graft as Bridging Stents in Experimental Fenestrated Endografting

Contact Info

Product

Resources

About