Features of Structure and Solidification of Extended Double Ingots for Hollow Forgings. Part 1

Rutskii, D. V.; Zyuban, N. A.; Chubukov, M. Yu.

doi:10.1007/s11015-016-0267-x

Cited by 5 publications

(3 citation statements)

References 2 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Examination of longitudinal and transverse sections of ingots reveals porosity and cracks in their central part. They have to be eliminated during the forging process [2,3]. Axial porosity is one of typical defects of conventional ingots.…”

Section: Literature Review and Problem Statementmentioning

confidence: 99%

Development of a new process for expanding stepped tapered rings

Марков¹,

Gerasimenko²,

Aliievа³

et al. 2019

EEJET

View full text Add to dashboard Cite

Досліджено новий спосіб розкочування великогабаритних конусних кілець зі ступінчастим профілем. Запропонований спосіб полягає у деформуванні заготівки з уступом східчастим бойком. Запропонована методика проведення досліджень методом скінчених елементів. Методика призначена для визначення залежностей напружено-деформованого стану та формозміна заготiвки у процесі розкочування східчастим бойком. Змінними параметрами були відносна висота виступу східчастих заготівок, яка варіювалась в інтервалі 2,2...2,5. На основі скінчено-елементного моделювання були встановлені: розподіл інтенсивності деформацій у перерізі поковки після розкочування ступінчастим бойком. Визначалась конусність поковок, яка утворюється при розкочуванні за даним способом. Результати скінчено-елементного моделювання перевірялися експериментальними дослідженнями на свинцевих та сталевих зразках. Була запропонована методика проведення експериментальних досліджень. Скінчено-елементне дослідження дозволило встановити, що розкочування ступінчастим бойком призводить до утворення поковки конусної форми. Це пояснюється тим, що при обтисканні уступу йде більша тангенціальна деформація кільцевої заготівки в зоні уступу, ніж зоні виступу внаслідок різної висоти ступінчастої заготівки. Результати скінчено-елементного моделювання були підтверджені експериментами в лабораторних умовах на свинцевих та сталевих зразках. Збільшення діаметру виступу заготівок призводить до збільшення ступеня деформації виступу, що викликає збільшення діаметра отвору виступу. Аналіз макроструктури конусної кільцевої поковки зі ступінчастим профілем дозволив встановити, що при використанні операції розкочування ступінчастого кільця східчастим інструментом волокна структури повторюють форму деталі, що виключає їх перерізання при механічній обробці. В результаті досліджень було встановлено, що розкочування ступінчастих конусних заготівок можливе, це розширює технологічні можливості процесу розкочування велико габаритних поковокКлючові слова: ступінчасте конусне кільце, розкочування, ступінчастий бойок, розподіл деформацій, формозміна, конусність UDC 621.735.3

show abstract

Section: Literature Review and Problem Statementmentioning

confidence: 99%

Development of a new process for expanding stepped tapered rings

Марков¹,

Gerasimenko²,

Aliievа³

et al. 2019

EEJET

View full text Add to dashboard Cite

show abstract

“…The high-alloy steels receive mounting attention in the iron and steel industry, due to its high added value in the manufacturing market. However, there are difficulties in the quality control of these steels due to their high carbon and alloy content, and hence high cracking susceptibility [5, 6, 7, 8, 9]. The high quality mould steel is produced after forging, which should qualify via flaw detection, high surface quality, and ±2HRC (Rockwell hardness) difference in hardness uniformity (between the surface and core).…”

Section: Introductionmentioning

confidence: 99%

Cracking and segregation in high-alloy steel 0.4C1.5Mn2Cr0.35Mo1.5Ni produced by thick continuous casting

Chu

Fan

et al. 2019

Heliyon

View full text Add to dashboard Cite

Based on our innovative application of using thick continuous casting slab 0.4C1.5Mn2Cr0.35Mo1.5Ni (high alloy) for the production of high-quality mould steel, the present study investigated the high cracking susceptibility of high-alloy steel and segregation in continuous casting slab. The thermal expansion and the continuous cooling transformation (CCT) curve measurement, together with a high temperature in situ observation, confirmed the martensite phase transition happening at approximately 583 K that would result in an increase in the hardenability and cracking susceptibility. The cracking susceptibility zone was determined by high-temperature mechanical properties measurement. The high-alloy mould steel has no II brittle zone, and III brittle zone is 973–1148 K. As a conclusion, the straightening temperature should be above 1148 K to avoid the cracking during the continuous casting. Moreover, the elemental segregation of carbon, sulfur, chromium, and molybdenum along the cracking was examined by electron probe microanalysis (EPMA) quantitative analysis that might be another reason for the steel crack formation. It shows that Martensite phase transition happened at approximately 583 K that would result in an increase in the hardenability and cracking susceptibility.

show abstract

“…Під час кристалізації звичайного злитка з'являються дефекти, такі як пористість, усадочна раковина, газові порожнини та ін. Аналіз результатів поздовжнього та поперечного розрізу злитків, що представлений у роботах [2,3] дозволив встановити, що у центрі заготовки розташовуються рихлощі та тріщині, які повинні бути усунуті в процесі кування.…”

unclassified

Дослідження Процесу Розкочування Ступінчастих Конусних Кілець

Gerasimenko¹,

Марков²,

Kosilov³

et al. 2019

ОМТ

View full text Add to dashboard Cite

Герасименко О. В., Марков О. Є., Косілов М. С., Хващинський А. С., Іванов П. П. Дослідження процесу розкочування ступінчастих конусних кілець // Обробка матеріалів тиском. – 2019. – № 1 (48). – C. 71 –76. В роботі досліджено новий спосіб розкочування крупногабаритних конусних кілець зі ступінчастим профілем. Запропонований спосіб полягає у деформуванні заготовки з уступом ступінчастим бойком. В роботі запропонована методика проведення досліджень методом скінчених елементів. Методика призначена для визначення залежностей напружено-деформованого стану та формозмінення заготовки у процесі розкочування ступінчастим бойком. Змінними параметрами були відносна висота виступу ступінчастих заготовок, яка варіювалась в інтервалі 2,3 ... 2,4. На основі скінчено-елементного моделювання були встановлені: розподіл інтенсивності деформацій у перерізі поковки після розкочування ступінчастим бойком. Визначалась конусність поковок, яка утворюється при розкочуванні за даним способом. Скінчено-елементне дослідження дозволило встановити, що розкочування ступінчастим бойком призводить до утворення конусної форми поковки. Це пояснюється тим, що при обтисканні уступу йде більша тангенціальна деформація кільцевої заготовки в зоні уступу, ніж зоні виступу внаслідок різної висоти ступінчастої заготовки. Встановлено, що при розкочуванні заготовки з різницею відносних діаметрів 0,43 виступ та уступ одночасно деформуються під час всього процесу розкочування. При цьому уступ інтенсивніше збільшується у діаметрі, ніж виступ, через що поковка набуває конусну форму. Це пояснюється різними ступенями деформації, які утворюються у виступі та уступі. Причому ступінь деформації в уступі збільшується інтенсивніше, ніж у виступі. Різниця у ступенях деформації виникає через різницю у товщині стінок виступу та уступу. В результаті досліджень, виконаних в роботі, було встановлено, що розкочування ступінчастих конусних заготовок можливе, це розширює технологічні можливості процесу розкочування крупногабаритних поковок.

show abstract

Features of Structure and Solidification of Extended Double Ingots for Hollow Forgings. Part 1

Cited by 5 publications

References 2 publications

Development of a new process for expanding stepped tapered rings

Development of a new process for expanding stepped tapered rings