Fatigue Stiffness Degradation Behaviour of Woven Composite π Joint

Abstract

Fatigue stiffness degradation behaviour of woven composite π joint subjected to tensile-tensile cycle loading is studied. Because of the complex structural configuration of woven composite π joints and a variety of failure modes, there exhibited four stiffness degradation modes in fatigue test. For example, stable slight reduction mode, abruptly decreasing mode, step decreasing mode and constant stiffness mode. Each stiffness degradation mode has a corresponding failure mode in fatigue test.