Faraday rotation and photoluminescence in heavily Tb3+-doped GeO2-B2O3-Al2O3-Ga2O3 glasses for fiber-integrated magneto-optics

Abstract

We report on the magneto-optical (MO) properties of heavily Tb3+-doped GeO2-B2O3-Al2O3-Ga2O3 glasses towards fiber-integrated paramagnetic MO devices. For a Tb3+ ion concentration of up to 9.7 × 1021 cm−3, the reported glass exhibits an absolute negative Faraday rotation of ~120 rad/T/m at 632.8 nm. The optimum spectral ratio between Verdet constant and light transmittance over the spectral window of 400–1500 nm is found for a Tb3+ concentration of ~6.5 × 1021 cm−3. For this glass, the crystallization stability, expressed as the difference between glass transition temperature and onset temperature of melt crystallization exceeds 100 K, which is a prerequisite for fiber drawing. In addition, a high activation energy of crystallization is achieved at this composition. Optical absorption occurs in the NUV and blue spectral region, accompanied by Tb3+ photoluminescence. In the heavily doped materials, a UV/blue-to-green photo-conversion gain of ~43% is achieved. The lifetime of photoluminescence is ~2.2 ms at a stimulated emission cross-section σem of ~1.1 × 10−21 cm2 for ~ 5.0 × 1021 cm−3 Tb3+. This results in an optical gain parameter σem*τ of ~2.5 × 10−24 cm2s, what could be of interest for implementation of a Tb3+ fiber laser.

Ultralarge magneto-optic rotations and rotary dispersion in terbium gallium garnet single crystal

“…For example, in a CaF 2 matrix, this wavelength is estimated at ≈225 nm [23]. Similarly, in various kinds of glass, the effective transition lies in the wavelength range of 218-234 nm [24] while in a recent study [25] on heavily doped Tb 3 ions in…”

Giant Faraday Rotation through Ultrasmall Fe0n Clusters in Superparamagnetic FeO‐SiO2 Vitreous Films

“…Especially for the higher contents of FeO, these absolute values exceed the previous benchmarks of Eu 2+ or Tb 3+ ‐containing glasses by up to two orders of magnitude. For example, the Verdet constant of 58.0EuO·12.0Al 2 O 3 ·20.0B 2 O 3 ·10.0SiO 2 is about −300 rad T −1 m −1 at 633 nm,11 and that of 17GeO 2 ·23B 2 O 3 ·32Al 2 O 3 ·28Tb 2 O 3 is −120 rad T −1 m −1 14. Instead, similarly high values have presently been known only for ferrimagnetic crystals such as YIG.…”

The influence of TeO2 on thermal stability and 1.53μm spectroscopic properties in Er3+ doped oxyfluorite glasses

“…In addition, good thermal stabilities are required for fiber drawing [20]. Also, a high T g means that the glass has good thermal stability to resist thermal damage at high power densities [19].…”