Failure Prediction and Surface Characterization of GFRP Laminates: A Study of Stepwise Loading

Abstract

The present study explores the failure and surface characteristics of Glass Fiber-Reinforced Polymers (GFRP). Stepwise loading was applied in this study to understand the multi-static loading effect on the laminates before final failure. The loading was set three times to reach 10 kN with loading–unloading movement before final load until failure. The results showed that the angle of the GFRP UD laminates’ position significantly impacts the system’s failure. The results were analyzed using theoretical calculation experiment analysis, and then the failure sample was identified using ASTM D3039 standard failure. The laminates with 0° layer on edge ([0/90]S laminates) underwent preliminary failure before final failure. The mechanism of stepwise loading can be used to detect the effect of preliminary failure on the laminates. The [0/90]S laminates are subjected to stress concentration on the edge due to fiber alignment and discontinued fibers in the 0-degree direction. This fiber then fails due to debonding between the fiber and the matrix. The laminates’ strength showed that [90/0]S specimens have an average higher strength with 334.45 MPa than the [0/90]S laminates with 227.8 MPa. For surface roughness, the value of Ra increases more than six times in the 0° direction and three times in the 90° direction. Moreover, shore D hardness showed that the hardness was decreased from 85.6 SD then decreased to 70.4 SD for [0/90]S and 65.9 SD for [90/0]S. The matrix debonding, layer delamination and fiber breakage were reported as the failure mode behavior of the laminates.

Development of Photoluminescent and Photochromic Polyester Nanocomposite Reinforced with Electrospun Glass Nanofibers

“…Fiber-reinforced polymeric composites have found widespread uses in several industries, including the construction of satellites, vehicles, and aeroplanes. Nanofiber-reinforced polymer nanocomposites [ 40 , 41 ] have attracted a lot of attention as viable materials for many fields. This could be attributed to the improved interfacial binding strength of the filler with the matrix, which is much improved due to the increased surface area of the integrated nanofibers.…”

Assessing Mechanical Properties of Jute, Kenaf, and Pineapple Leaf Fiber-Reinforced Polypropylene Composites: Experiment and Modelling

“…The past few decades have seen the emergence of natural fibers in our daily commodities, in their basic forms or in other geometric textile structures such as yarns, fabrics, and non-woven sheets, as the alternative reinforcements to create composite materials due to the ecological advantages as they offer over the manmade fibers such as glass or carbon fibers [ 1 , 2 , 3 , 4 , 5 , 6 , 7 ]. Among the natural fibers, few members of the subgroup of bast fibers such as jute, flax, hemp, kenaf and ramie, and few members of the subgroup of leaf fibers such as sisal and pineapple have attracted particular attention from both the industry and academia.…”

Recent Progress on Natural Fibers Mixed with CFRP and GFRP: Properties, Characteristics, and Failure Behaviour

“…When the components of natural fiber composite are all biobased, composites can rapidly decompose naturally in the environment at the end of their life cycle [ 9 ]. Composite material also can be produce with synthetic fibers, such as glass, carbon, aramid, and kevlar [ 10 , 11 , 12 ]. Composites often use synthetic fibers as reinforcement.…”