Fabrication of gold nano-particle based sensors using microspotting and DEP technologies

Abstract

Abstract:We have shown that Au nanoparticles (Au NPs) pearl chain could be formed consistently between microelectrodes by combining microspotting and DEP technologies. Experimental results on varying the Au particle size and dielectrophoretic (DEP) parameters, including voltage and frequency, are reported in this paper to explore the critical parameters in controlling the Pearl Chain Formation (PCF) process between microelectrodes. PCF was observed from 10kHz to 5MHz for 100nm Au NPs, and 100kHz to 10MHz for 10nm Au NPs. Variations in formation rate were detected when the applied voltage and particle size varied. With higher voltage, pearl chain began to form at higher rate and the formation time decreased. The optimum frequency of the Au NPs PCF shifted to higher frequency region when the particle size decreased. Theoretical analysis was carried out by applying the theories of DEP force and AC electrokinetics to explain the observations with the DEP frequency ranging from 10 Hz to 10MHz. Finally, Au nanoparticle chains formed between the microelectrodes were shown to vary in resistance when environmental temperature was changed, indicating that these Au particle sensors could potentially be used to sense temperature and other thermal-based physical phenomena.

Dielectrophoretic assembly of 2 nm gold particles for nano-sensing applications

“…After bridging the electrode gap, the nanoparticle wires were demonstrated by our group to sense thermal based physical phenomena, e.g. airflow sensing, the same as the previous experimentation with the larger gold nanoparticles (10 nm and 100 nm) [17]. However, the 2 nm gold particles are expected to obtain superior sensitivity and consume lower power in nano-sensing applications, which still under the investigation.…”