Fabrication and Frosting Properties Study of Surface-Active Agents Coating Based on Nanoporous Aluminum Substrate

Abstract

In order to solve the frosting and blockage problem of an air conditioning evaporator’s fin in winter, the nanoporous aluminum plates with low surface energy has been proposed in this paper, which are fabricated by an anodizing method and then modified by lauric acid. The nanoporous aluminum plates with different nanoporous diameters ranging from 15 nm to 400 nm are obtained by changing the magnitude of the oxidation current. The surface contact angle of the nanoporous aluminum plates is an important factor influencing its surface frost and condensation. The test results show that the surface contact angle is decreased with the increasing of nanoporous diameter. When the nanoporous aluminum plates are modified by lauric acid, the contact angle is proportional to the nanoporous diameter, and the maximum contact angle can reach about 171°. A set of experimental instruments has been set up to simulate the typical winter climate in northern China, and the frosting properties of the nanoporous aluminum plate’s fin is analyzed by experiment. The results show that increasing the contact angle of aluminum plates can effectively improve its anti-frosting properties. The average frosting rate of the aluminum plate with the contact angle of 60° is about 0.33 [g/(min∙m2)], which is 1.74 times that of the aluminum plate with the contact angle of 171°, whose frosting rate is about 0.19 [g/(min∙m2)]. After taking the expanded aperture processing to the aluminum plate, the diameter with 30 nm, 100 nm, 200 nm, 300 nm, and 400 nm nanoporous aluminum plates are obtained and the polished aluminum plates are also prepared for comparing. Through the test results, the nanoporous aluminum plates are shown to have anti-frosting properties, and the nanoporous aluminum plates with diameter of 300 nm are shown to have the best anti-frosting properties. The calculation mode of frosting growth is derived on the base of experimental results. This research will be helpful in indicating the potential research area of the low-carbon-emission and energy-saving technology for the researchers all over the world.

A Review of Methods and Techniques for Detecting Frost on Plant Surfaces

“…Compared with other frost events such as airplane wing and track frosting, etc. [38][39][40][41][42][43], frost detection based on plant surfaces has inevitably increased in specificity due to the diversity of plant types, including the surface characteristics and cold tolerance of different plants. Frosting on leaf surfaces is a time-varying dynamic quantification process with relatively dispersed distribution.…”