Experimental Investigation of the Three-Point Bending Property of a Sandwich Panel with a Metal Rubber Core

Abstract

Sandwich structures and porous materials have been applied widely in various fields due to their excellent mechanical performance, and multifunctional composites will have a significant engineering demand in the future. Studying damped composites’ mechanical properties and failure forms has significant engineering value and significance. However, the current connecting processes for sandwich panels and porous materials must be improved. Therefore, to explore the ambiguity of the connection interface between the core material and panel in sandwich panels, as well as the mechanical properties of such structures, a sandwich panel with a metal rubber core material was prepared using vacuum brazing and cementing processes. Microscopic examinations using scanning electron microscopy and energy-dispersive spectroscopy were conducted to observe the physical bonding mechanism at the interface of the sandwich panel. The results indicate that the brazed sandwich panels exhibited a more uniform and continuous interface than the cemented sandwich panels. This work designs three-point bending compression experiments to investigate the effects of core material thickness, density, and preparation process on the bending mechanical properties of the sandwich panel. Failure modes of the sandwich panel during the experiments are analyzed. The experimental results show that the failures of the brazed sandwich panels are attributable to the bending deformation of the panel and the shear failure of the metal wire core material. The cemented sandwich panels exhibit separation failures in the area below the indenter and at both ends of the panel. The core material’s thickness and density significantly influence the bending performance of the sandwich panels. An increase in the core material’s thickness and density effectively enhances the sandwich panels’ peak load and energy absorption capacity.