This research article reveals the effect of Dy +3 substitution on ?-ferrites KFe 11-x Dy x O 17 with composition (x=0.00, 0.25, 0.50, 0.75 and 1.0). The samples were synthesized by sol-gel auto- combustion method, sintered at 950 o C temperature. The XRD patterns confirmed the single phase of the synthesized samples. The crystallite size varied in the range of 21.49 nm to 25.24 nm for all samples. The polarization verses electric field (P-E) loops indicated the loosy behavior in all samples. The lossy behavior of the samples was seemed to be increased up to x=0.5 and then decreased. The theoretical expression was used to fit an upper branch of P-E loops. FT-IR spectra showed absorption bands at different wavenumbers due to M-O-M stretching vibrations, H-O-H stretching, and C-O-C stretching vibrations, which also confirmed the formation of the single-phase in the samples. Electrochemical measurements of synthesized nano ferrites were carried out by using cyclic voltammetry in a 3.0 M KOH solution. Electrochemical impedance spectroscopy (EIS) has been described by Nyquist plots.
“…Compared with the real un-mingled sample, the substituted rareearth sample shows high lossy behavior. The concentration up to X=0.50 is due to the increase in the resistive nature of the material [19]. For a pure sample (X=0.0), the value of Ps and Pr is maximum, showing conductive nature.…”
This research article reveals the effect of Dy +3 substitution on ?-ferrites KFe 11-x Dy x O 17 with composition (x=0.00, 0.25, 0.50, 0.75 and 1.0). The samples were synthesized by sol-gel auto- combustion method, sintered at 950 o C temperature. The XRD patterns confirmed the single phase of the synthesized samples. The crystallite size varied in the range of 21.49 nm to 25.24 nm for all samples. The polarization verses electric field (P-E) loops indicated the loosy behavior in all samples. The lossy behavior of the samples was seemed to be increased up to x=0.5 and then decreased. The theoretical expression was used to fit an upper branch of P-E loops. FT-IR spectra showed absorption bands at different wavenumbers due to M-O-M stretching vibrations, H-O-H stretching, and C-O-C stretching vibrations, which also confirmed the formation of the single-phase in the samples. Electrochemical measurements of synthesized nano ferrites were carried out by using cyclic voltammetry in a 3.0 M KOH solution. Electrochemical impedance spectroscopy (EIS) has been described by Nyquist plots.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.