Estudo comparativo da corrosão de agregados de MgO, com diferentes microestruturas e purezas, por escória de aciaria LD.

Abstract

High quality materials are increasingly desired by consumers, and advances in technologies of steelmaking processes are closely linked to manufacturing suitable high performance refractories which do not interfere in the final properties of materials produced. Magnesia-carbon refractories are widely used in several steelmaking plants, both for transportation and refining processes which makes the knowledge of the quality of raw materials is essential for manufacturing high quality refractories. In this work, the approach is the study of how the corrosion behavior of magnesia aggregates (sinterized and electrofused) by LD steelmaking slag occurs using a modified crucible testing. The magnesia aggregates were characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). The XRF analysis shows that the main impurities of magnesia grains is CaO and SiO2 and the SEM analysis showed their impurities are concentrate on grain boundary in electrofused magnesia, while it is found throughout the sinterized magnesia aggregates. The major phase found both magnesia aggregates is periclase. The largest grain sizes were found in ME3 samples, while the smaller sizes in ME1. The slag used comes from converter (BOF) and has high concentration of FeO. The corrosion tests showed that the attack on magnesia aggregates occurred, mainly by the infiltrating of iron compounds in the grain boundary, dragging the grains to the bath and dissolving them into slag. Among the electrofused, the performance could be estimated in ME3>ME2>ME1. The performance for sinterized would be as follows MS3>MS1>MS2.