Engineering the degree of concavity of one-dimensional Au–Cu alloy nanorods with partial intermetallic compounds by facile wet chemical synthesis

Cu-based nanocrystals are desirable for high efficiency catalysis, although they are easily oxidized under ambient conditions. Alloying Au and Cu provides the strategy for Cu-contained nanocrystals toward both high stability and high catalytic activity. However, a synthetic method of homogeneous alloy nanocrystals with tunable composition in aqueous solutions is lacking. Specific composition for achieving both enhanced stability and high catalytic activity remains elusive. Herein, coreduction of Au 3+ and Cu 2+ was performed through controlling the kinetics of the coreduction to form AuCu alloyed shells on the Au nanorod (NR) cores and obtain Au@AuCu NRs under the protection of nitrogen. The Cu atomic fraction (atom %) of the shell was finely tuned from 0 to 100% by controlling the fraction of Cu 2+ cations in the growth solution. For Au@Au 0.85 Cu 0.15 NRs, epitaxial growth of AuCu alloy on the Au NR was evidenced with about 4.0% lattice mismatch due to Cu alloying in the Au lattice by high-resolution transmission electron microscopy. Au@AuCu NRs with different aspect ratios were also obtained for tuning longitudinal plasmonic resonance. Stability characterization indicates that the Au@AuCu NRs with Cu atom % in the shell lower than 15% are of enhanced stability, while an increase in Cu atom % in the shell from 0 to 15.3 and 100% leads to dramatic reduction of the activation energy, E a , of p-nitroaniline from 111 to 45 and 33 kJ/mol, respectively. Therefore, Au@Au 0.85 Cu 0.15 NRs are preferable for high catalytic activity and enhanced stability.

show abstract

scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.

Contact Info

hi@scite.ai

10624 S. Eastern Ave., Ste. A-614

Henderson, NV 89052, USA

Blog Terms and Conditions API Terms Privacy Policy Contact Cookie Preferences Do Not Sell or Share My Personal Information

Made with 💙 for researchers

Part of the Research Solutions Family.

Engineering the degree of concavity of one-dimensional Au–Cu alloy nanorods with partial intermetallic compounds by facile wet chemical synthesis

Abstract: Fine-modulating morphology of bimetallic nanomaterials plays a vital role in enhancing their catalytic activity. Among the various morphologies, concave structures have received considerable attention due to the features of three...

Cited by 2 publications

References 49 publications

Rational design of noble metal-based multimetallic nanomaterials: A review

Rational design of noble metal-based multimetallic nanomaterials: A review

Room-Temperature Synthesis of Au@AuCu Alloyed Nanorods in Aqueous Solutions for High Catalytic Activity and Enhanced Stability

Contact Info

Product

Resources

About