Electrophoretic deposition of BaTi0.85Zr0.15O3 nanopowders

Abstract

The present study reports the results of thick films (20-130 µm) produced through electrophoretic deposition of BaTi 0.85 Zr 0.15 O 3 (BTZ) nanometric powders synthesized by the Pechini's method. The BTZ powderscalcined at 600°C/2h presented a single crystalline phase with an average particle size of ~20nm. To thick films deposition, a stable suspension of acetylacetone (Acac) and ethanol (EtOH)was prepared and the powder was deposited on platinum substrates. The viscosity of BTZ powders suspensions as a function of operational pH (OpH)was measured and the reactions between nanoparticles and the media were discussed. A milling process was used to deagglomerate the powders and it had a great influence in the suspension stability and deposition of thick films. Dense and crack-free thick films were obtained after sintering at 1220 °C/1h. The dielectric properties results, comparable with those of bulk BTZ ceramics, suggested potential applications of the EPD process for the deposition of ferroelectric/piezoelectric thick films.

Kesan Pemendapan Elektroforesis Gam Arab terhadap Halaju Kakisan pada Aluminium 5052

“…Kajian menggunakan EPD ini adalah lebih selamat dan mudah untuk digunakan jika dibandingkan dengan kaedah salutan lain seperti pemendapan wap fizikal, pemendapan wap kimia dan penyemburan (Feng et al 2013;García & Smit 2006;Pech-Rodríguez et al 2014). Proses EPD menghasilkan molekul yang melarut dalam larutan akueus atau organik yang dipindahkan ke elektrod apabila dialirkan arus elektrik (Antonelli et al 2013;Garcia et al 2006;Pech et al 2014;Peter & Sanjay 2015;Raddaha et al 2014). Bagi mencapai deposit struktur zarah elektroforetik yang seragam mengikut ia bergantung kepada jumlah kepekatan larutan, pH dan kekonduksian gam Arab.…”

Effect of Arabic Gum Electrophoresis Desposition on Corrosion of SS316L in Acidic

“…Kaedah ini adalah lebih selamat dan mudah untuk dilakukan berbanding dengan kaedah salutan konvensional yang lain, antaranya seperti pemendapan wap fizikal, pemendapan wap kimia, dan penyemburan (Feng et al 2013;García & Smit 2006;Pech-Rodríguez et al 2014). Proses EPD menghasilkan molekul yang melarut dalam larutan akueus atau organik yang dipindahkan ke elektrod yang dikenakan di bawah tindakan medan elektrik terpakai (Antonelli et al 2013). Kaedah EPD bertujuan untuk mencapai salutan yang sekata pada permukaan logam, kepekatan larutan yang dipakai, voltan dan arus juga merupakan faktor lain yang perlu diambil kira.…”