Electrokinetic properties of polypropylene‐layered silicate nanocomposite fibers

Abstract

Nanocomposite fibers based on polypropylene (PP) polymer were prepared with different content of nanofiller. Filaments were spun from an isotactic iPP homopolymer. Montmorillonite modified by N,N-dimethyl-N,N dioctadecylammonium cations was used for preparation of PP nanocomposite fibers. A PP grafted with acrylic acid was added as a coupling agent. Nanocomposite fibers were characterized, i.e., the surface morphology of PP nanocomposite fibers was observed and surface properties were defined by electrokinetic properties determination by zeta potential measurements. For particle distribution observation the plasma etching was involved as a method for sample preparation. The addition of nanoparticles has an impact on ZP value of nanofilled fibers, however, isoelectric point IEP is not significantly influenced by different concentrations of nanofiller.

Estudo de nanocompósitos formados por PLA e nanopartículas de celulose.

“…Quando o valor do potencial Zeta está nesta zona, ou seja, esta em equilíbrio, a partícula tem mesma afinidade pelos íons hidroxônio e hidroxila. [137,138] Nota-se que em todas as amostras o Potencial Zeta manteve-se próximo a zero e a variação do pH não alterou significativamente os valores, exceto nas extremidades da curva. Porém, para valores de pH tão extremos é possível que esteja havendo a desintegração das partículas, resultando em uma mudança no valor de Zeta.…”

“…Porém, para valores de pH tão extremos é possível que esteja havendo a desintegração das partículas, resultando em uma mudança no valor de Zeta. [125,137,138] Para verificar a diferença entre as superfícies, foram realizados o ensaio de potencial Zeta de partículas de NC obtidas por hidrólise com ácido sulfúrico e de partículas do papel filtro, basicamente composto por celulose. As curvas obtidas estão apresentadas na Figura 33.…”