Electrodeposited nickel–graphene nanocomposite coating: influence of graphene nanoplatelet size on wear and corrosion resistance

Hau, Tran Van; Trinh, Pham Van; Tú, Nguyễn Văn; Duoc, Phan Nguyen Duc; Phuong, Mai Thi; Toan, Nguyen Ngoc; Phuong, Doan Dinh; Nam, Nguyen Thanh; Lãm, Vũ Đình; Minh, Phan Ngoc; Thắng, Bùi Hùng

doi:10.1007/s13204-021-01780-0

Cited by 12 publications

(3 citation statements)

References 37 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Các vật liệu nano cácbon như graphene (Gr), ống nano cácbon (CNTs) có các tính chất lý hóa rất đặc biệt nên có nhiều tiềm năng ứng dụng trong các lĩnh vực như cảm biến [1], tụ điện [2], transistor [3] và vật liệu gia cường chống ăn mòn điện hóa [4]. Graphene là màng mỏng hai chiều với độ dẫn điện rất cao, độ bền cơ học cao và độ linh động điện tử lớn [5].…”

Section: đặT Vấn đềunclassified

Chế Tạo Và Tính Chất Của Vật Liệu Tổ Hợp Graphene – Ống Nano Cácbon – Hạt Nano Vàng

Phan¹,

Phan²,

Cao³

et al. 2022

hueuni-jns

View full text Add to dashboard Cite

Trong công trình này, màng tổ hợp của vật liệu graphene (Gr) – ống nano cácbon hai tường (DWCNT) và hạt nano kim loại vàng (AuNPs) (DWCNT-AuNPs-Gr) đã được chế tạo bằng phương pháp lắng đọng pha hơi nhiệt hóa học (CVD). Hình thái học bề mặt và các tính chất điện, điện hóa của vật liệu tổ hợp đã được khảo sát thông qua kính hiển vi điện tử quét phát xạ trường, phổ Raman, điện trở bốn mũi dò và kỹ thuật quét thế vòng (CV). Với nồng độ DWCNTs 0,3 g/L và tốc độ quay phủ 4000 vòng/phút, vật liệu DWCNTs-AuNPs-Gr có điện trở bề mặt giảm 2,3 lần so với màng Gr và đạt khoảng 549 W/sq; dòng đỉnh đáp ứng trong dung dịch 2 mM K3[Fe(CN)6]/K4[Fe(CN)6] trong 0,1 M PBS đạt 15,79 µA tại 50 mV/s, cao gấp 1,48 lần so với điện cực biến tính màng Gr và gấp 2,57 lần so với điện cực trần. Vật liệu DWCNTs-AuNPs-Gr có tiềm năng ứng dụng trong cảm biến điện hóa để phát hiện các phần tử sinh học khác nhau.

show abstract

Section: đặT Vấn đềunclassified

Chế Tạo Và Tính Chất Của Vật Liệu Tổ Hợp Graphene – Ống Nano Cácbon – Hạt Nano Vàng

Phan¹,

Phan²,

Cao³

et al. 2022

hueuni-jns

View full text Add to dashboard Cite

show abstract

“…The results indicate that GNPs had enhanced the wear and corrosion resistance of the nickel composites coating, further, the size of GNPs also plays a crucial role. The wear resistance and corrosion resistance were premier for GNP which was ball milled for 5 h [19].…”

Section: Introductionmentioning

confidence: 99%

Flexural and corrosion behaviour of WC-10Co-4Cr + Graphene sprayed on textured HSLA-steel

Shrivastava

Kumar

Verma

et al. 2023

Surface Engineering

View full text Add to dashboard Cite

The aim of this work was to investigate the flexural strength and corrosion behaviour of graphene-reinforced WC-10Co-4Cr HVOF coating on sandblasted and laser-textured DH-36 naval-grade steel. In this regard, WC-10Co-4Cr and WC-10Co-4Cr + 3% graphene nanoparticles (GNPs) are applied on DH-36 substrates using the HVOF coating technique and their microhardness, flexural strength and corrosion behaviour are investigated. Amongst all, the flexural strength of WC-10Co-4Cr + 3%GNPs coating on laser-textured sample with pitch-to-diameter (p/d) ratio 2 was minimum (327.006 MPa) due to the effect of GNPs and better mechanical interlocking at the coating-substrate interface. Also, the corrosion resistance of coated DH-36 steel was evaluated by salt spray test; it revealed that corrosion resistance was improved with the application of WC-10Co-4Cr coating, which was further enhanced by the addition of GNPs as GNP has the property of being impermeable to gasses and salts. Further, microstructures and morphologies of the corroded surface were investigated using FE-SEM images.

show abstract

“…To address this issue, many researchers have dedicated themselves to developing a large number of alternative materials to facilitate the application of epoxy coatings in the corrosion field. Among these, graphene, with its high tensile strength (130 GPa) [ 21 ], is an effective reinforcement material in polymer matrices and has attracted extensive research interest among scholars in the field of corrosion due to its natural stratified structure [ 22 ]. For example, Tian et al modified GO with quaternary ammonium compounds to enhance the anti-corrosion performance of epoxy coatings.…”

Section: Introductionmentioning

confidence: 99%

Corrosion Resistance of CeO2-GO/Epoxy Nanocomposite Coating in Simulated Seawater and Concrete Pore Solutions

Liu

Lyu

et al. 2023

Polymers

View full text Add to dashboard Cite

Reinforced concrete structures in the marine environment face serious corrosion risks. Coating protection and adding corrosion inhibitors are the most economical and effective methods. In this study, a nano-composite anti-corrosion filler with a mass ratio of CeO2:GO = 4:1 was prepared by hydrothermally growing cerium oxide on the surface of graphene oxide. The filler was mixed with pure epoxy resin at a mass fraction of 0.5% to prepare a nano-composite epoxy coating. The basic properties of the prepared coating were evaluated from the aspects of surface hardness, adhesion grade, and anti-corrosion performance on Q235 low carbon steel subjected to simulated seawater and simulated concrete pore solutions. Results showed that after 90 days of service, the corrosion current density of the nanocomposite coating mixed with corrosion inhibitor was the lowest (Icorr = 1.001 × 10−9 A/cm2), and the protection efficiency was up to 99.92%. This study provides a theoretical foundation for solving the corrosion problem of Q235 low carbon steel in the marine environment.

show abstract

Electrodeposited nickel–graphene nanocomposite coating: influence of graphene nanoplatelet size on wear and corrosion resistance

Cited by 12 publications

References 37 publications

Chế Tạo Và Tính Chất Của Vật Liệu Tổ Hợp Graphene – Ống Nano Cácbon – Hạt Nano Vàng

Chế Tạo Và Tính Chất Của Vật Liệu Tổ Hợp Graphene – Ống Nano Cácbon – Hạt Nano Vàng

Flexural and corrosion behaviour of WC-10Co-4Cr + Graphene sprayed on textured HSLA-steel