Effects of iron concentration and redox states on failure of boron-free E-glass fibres under applied stress in different conditions

Wang, Qingwei; Brow, Richard K.; Li, Hong; Ronchetto, Erica Ann

doi:10.1007/s12034-017-1418-9

Cited by 1 publication

(2 citation statements)

References 19 publications

(20 reference statements)

Supporting

Mentioning

Contrasting

Order By: Relevance

“…The chemical durability was assessed by leaching tests [18] conducted in 1–3 mol/L HCl solutions and 0.5–1.5 mol/L NaOH solutions at 90 °C for 12 h.…”

Section: Methodsmentioning

confidence: 99%

“…A fundamental understanding of the effect of the iron redox ratio on the mechanical and chemical properties of basalt fiber is critically needed to guide new product development and associated economics of the basalt fiber industry [18], including the control of batch material and melting atmosphere. In this work, continuous basalt fibers were successfully prepared.…”

Section: Introductionmentioning

confidence: 99%

See 1 more Smart Citation

Effect of the Iron Reduction Index on the Mechanical and Chemical Properties of Continuous Basalt Fiber

et al. 2019

Self Cite

View full text Add to dashboard Cite

Basalt glass belongs to the iron-rich aluminosilicate glass system; thus, the iron content and the iron redox index (IRI=Fe2+/Fetotal) influence the viscosity, density, mechanical and chemical properties of basalt fiber (BF). In this work, continuous BFs with IRIs ranging from 0.21–0.87 were prepared by adding a different amount of redox agents. An economical and easily accessible testing method—the spectral photometric method with 1,10-phenanthroline—is applied to measure the IRI with convinced accuracy, which has been approved by Mössbauer spectra and X-ray fluorescence analysis. The tensile strength of the BF samples increases approximately linearly with increasing IRI as a function of σ = 227.9 IRI + 780.0 . The FT-IR results indicate that, with increasing IRI, the ferric ions are replaced by the much stronger network formers (Al3+ and Si4+), hence the increased the tensile strength. The X-ray diffraction results show an amorphous nature of BF samples. Moreover, the tensile strength is significantly decreased after the alkali corrosion, which is partly attributed to the severe surface damaging according to the SEM results. This work proved the feasibility of mechanical property improvement in BF production by controlling the iron redox index.

show abstract