Effect of ZnO Mass on Nanostructure, Magnetic and Optical Properties of Fe2O3/MWCNT/ZnO Nanocomposites

Abstract

Fe2O3/MWCNT/ZnO nanocomposites were successfully synthesized through the precipitation method. The synthesis was carried out through a variation of ZnO mass, with (Fe2O3/MWCNT):ZnO mass ratio of 1:0, 1:0.5, 1:1, 1:1.5, and 0:1. The XRD analysis results suggested that the nanocomposites were composed of two phases, namely Fe2O3 with centered hexagonal structure and ZnO with hexagonal wurtzite structure. The ZnO diffraction peak tended to increase following the increasing ZnO composition within the nanocomposites. The presence of MWCNT was confirmed by the FTIR results signifying the detection of C=C vibration at wavenumbers of 1631-1640 cm -1 . The crystallite size of Fe2O3 and ZnO was in the range of 30.97-31.12 nm and 30.46-35.64 nm, respectively. The nanocomposites were comprised of the spherical, tube, and sheet particles, representing Fe2O3, MWCNT, and ZnO, respectively, with particle size ranged from 33.97 nm to 55.19 nm. The nanocomposites were observed to present weak ferromagnetic, with a decrease in saturation magnetization value following the increase of ZnO composition. The optical properties of the nanocomposites tended to decrease as the increasing ZnO composition.

MWCNTs/Fe2O3:ZnO Nanocomposite Material for Chemoresistive Sensing of Hydrogen Peroxide Vapors

“…The melting point of the hematite is in the range 1475–1565 °C with a density of 5.242 g/cm 3 . ZnO is also distinguished by its unique physicochemical properties such as a large excitation binding energy of 60 meV, high electron mobility of 400 cm 2 V –1 s –1 , and wide band gap energy of 3.37 eV. − …”