Effect of TPMS reinforcement on the mechanical properties of aluminium–alumina interpenetrating phase composites

Abstract

Triply Periodic Minimal Surface (TPMS)-based aluminium–alumina Interpenetrating Phase Composites (IPCs) manufactured through the combination of Additive Manufacturing (AM) and investment casting are explored in this study. Multiple alumina TPMS structures (Gyroid, Diamond, and Primitive) with different geometries and volume fractions were designed and fabricated using Digital Light Processing (DLP) AM technology. Afterwards, these ceramic structures were filled with an aluminium alloy via investment casting, uncovering an aluminium–alumina IPCs. A global characterization was performed, including ceramics shrinkage and mass loss; specimens’ morphology; chemical and crystalline characterization; density analysis and mechanical testing. Overall, DLP technology was found effective for producing these highly complex ceramic structures, with high surface quality. The sintered alumina structures presented a relative density of ca. 76.3% and a pseudo-ductile layer-by-layer failure behaviour, with Diamond-based TPMS exhibiting the highest compressive strength. Regarding the IPCs, the addition of aluminium significantly changed the compressive behaviour of the samples, presenting an energy absorption behaviour. The integration of the alumina phase into the aluminium alloy led to an improvement on the compressive offset stress of approximately 6% when compared to the aluminium alloy used. Diamond and Gyroid IPCs demonstrated similar mechanical behaviour and the highest mechanical performance. Graphical Abstract