Effect of surface topography and wettability on shear bond strength of Y-TZP ceramic

Abstract

Zirconia ceramics have been widely used as dental restorations due to their esthetic appearance and high flexural strength. The bonding of zirconia with resin cement should rely on both mechanical and chemical bonds. This study was performed to investigate the effect of zirconia surface topography and its wettability after surface pretreatments on the microshear bond strength (μSBS) of a resin cement. Zirconia slabs were prepared and randomly divided into 5 groups based on the surface treatment as follows: no treatment (control), air abrasion (AB), etching with hydrofluoric acid (F), the mixture of hydrofluoric acid and nitric acid (FN), or the mixture of hydrochloric acid and nitric acid (CN) for 10 min. The specimens were subjected to investigation of surface roughness characteristics [average roughness (Ra), peak-to-valley average distance (Rpv), skewness (Rsk), and kurtosis (Rku)] using atomic force microscopy (AFM) and measurements of surface contact angle (θc) and μSBS of a resin cement. In addition, the area % of the nanoscale surface irregularity (nSI%) was calculated from the AFM images. The effects of nSI%, Ra and θc on the μSBS were analyzed by multiple linear regression analysis (p < 0.05). Multiple regression analysis revealed that the nSI% was the most predominant factor for the μSBS (p < 0.001). A surface with larger nSI%, higher Ra and relatively lower θc was essential for establishing a reliable resin-zirconia bond.

Bond Strength of Milled and Printed Zirconia to 10-Methacryloyloxydecyl Dihydrogen Phosphate (10-MDP) Resin Cement as a Function of Ceramic Conditioning, Disinfection and Ageing

“…Studies in which neither increasing Al 2 O 3 particle size [42] nor increasing air abrasion pressure [10,36] resulted in increased bond strength when used with an MDP-containing cement or primer provide evidence that absolute roughness might be of minor importance. This assumption is also supported by the results of a recently published study, which showed that not R a but the presence (area %) of nanoscale surface irregularities was the most predominant factor for the strength of the resin-zirconia bond [43].…”