Effect of porosity on the absorbed, reemitted and transmitted light by a geopolymer metakaolin base

Gasca-Tirado, José Ramón; Rubio-Ávalos, J.C.; Muñiz-Villarreal, M.S.; Manzano-Ramı́rez, A.; Reyes-Araiza, José Luis; Sampieri-Bulbarela, S.; Villaseñor‐Mora, Carlos; Pérez-Bueno, J.J.; Apátiga, L.M.; Amigó, V.

doi:10.1016/j.matlet.2010.12.003

Cited by 20 publications

(3 citation statements)

References 8 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Geopolymers have been used in pervious concrete preparation and are an alternative binder material to Portland cement [28,29]. Zhou et al [30] used an alkaline activator at 40%, a mass ratio of 1:5 between the geopolymer binder material and a coarse aggregate, and a mass ratio of 0.35 between the alkali activator solute (sodium hydroxide and sodium silicate) and metakaolin.…”

Section: Introductionmentioning

confidence: 99%

Corrosion of Steel Rebars in Construction Materials with Reinforced Pervious Concrete

Lerma Villa,

Reyes Araiza,

Pérez Bueno

et al. 2024

Infrastructures

View full text Add to dashboard Cite

Pervious concrete has great potential for use in many practical applications as a part of urban facilities that can add value through water harvesting and mitigating severe damage from floods. The construction and agricultural industries can take direct advantage of pervious concrete’s characteristics when water is a key factor included in projects as part of the useful life of a facility. Pervious concrete also has applications in vertical constructions, fountains, and pedestrian crossings. This work evidences that pervious concrete’s corrosion current increases with increasing aggregate size. Also, corrosion is a factor to consider only when steel pieces are immersed, aggravated by the presence of chlorine, but it drains water and does not retain moisture. Steel-reinforced pervious concrete was studied, and the grain size of the inert material and the corrosion process parameters were investigated. The electrochemical frequency modulation technique is proposed as a suitable test for a fast, reproducible assessment which, without damaging reinforced cement structures, particularly pervious concrete, indicates a trend of increasing corrosion current density as the size of the aggregate increases or density diminishes.

show abstract

Section: Introductionmentioning

confidence: 99%

Corrosion of Steel Rebars in Construction Materials with Reinforced Pervious Concrete

Lerma Villa,

Reyes Araiza,

Pérez Bueno

et al. 2024

Infrastructures

View full text Add to dashboard Cite

show abstract

“…Geopolymers contain thermally activated natural materials (e.g., kaolinite clay) or industrial by-products (e.g., fly ash or slag). In addition, they have properties such as high compressive strength, low shrinkage, slow or fast setting, fire resistance, and low thermal conductivity [21,[30][31][32][33][34].…”

Section: Introductionmentioning

confidence: 99%

Geopolymeric Composite Materials Made of Sol-Gel Silica and Agroindustrial Wastes of Rice, Barley, and Coffee Husks with Wood-Like Finishing

et al. 2022

View full text Add to dashboard Cite

Geopolymers have been mainly utilized as structural materials; their chemical structure and morphologies have been explored for their potential as a high-performance material in emerging applications. Geopolymer composites reinforced with materials based on agro-waste are attracting interest in engineering applications due to their easy processing, low cost, low density, and high strength-to-weight ratio. This investigation pursues an experimental methodology that consists of a scheme to make composites with a geopolymer matrix and agro-waste (rice husk, barley, and coffee) as aggregate material, that can be applied in various fields of construction. The study was intended to determine the influence of adding various agro-wastes on the mechanical properties of the geopolymer. According to the respective ASTM standards, the materials obtained were prepared and analyzed to determine their compressive strength, flexural strength, hardness and scanning electron microscopy (SEM)-determined characteristics. The results revealed that, for the compression tests, the composites formed by a sol-gel matrix and barley husk showed a better yield, obtaining the highest value of 3.5 N/mm2. Concerning hardness testing, the composites with a geopolymer matrix and coffee husks obtained higher values compared to the other composites. For the flexural tests, the compounds with the sol-gel/fly ash matrix obtained the highest yield stress value, which was 5.25 MPa with an elastic modulus of 7.59 GPa. The results of the microstructural analysis showed good husk-matrix interaction, together with failure mechanisms. The conformation of such waste-based compounds may enable them to replace natural wood in some applications, such as in the finishing of interiors of homes, during the final stages in the construction of buildings, or in the decoration of inhabited houses, as well as in finishing in the manufacture of furniture.

show abstract

“…Οι Gasca-Tirado et al [210] ασχολήθηκαν με τις οπτικές ιδιότητες γεωπολυμερών με τη βοήθεια μετρήσεων UV/Vis που συντέθηκαν σε τρεις διαφορετικές θερμοκρασίες ωρίμανσης (40, 60 και 90°C) συσχετίζοντας τη μεγαλύτερη φωταύγεια που παρατηρήθηκε στα γεωπολυμερή που παρασκευάστηκαν σε θερμοκρασία ωρίμανσης 90°C με το μεγάλο πορώδες τους [182]. Επίσης μελετήθηκε η χρήση των γεωπολυμερών στη φωτοκατάλυση [211] όπου αναπτύχθηκε μέθοδος ιοντοεναλλαγής στο γεωπολυμερικό πλέγμα ώστε να συμπεριληφθεί το φωτοενεργό ΤiO 2 παρατηρώντας ότι o εγκλωβισμός του ανατάση στις κοιλότητες (σπηλαιώσειςcavities) εντός του γεωπολυμερούς διαταράσσει το γεωπολυμερικό πλέγμα καθώς και η ποσότητά του διαφέρει στα δείγματα ως συνάρτηση των συνθηκών της ιοντοεναλλαγής.…”

Section: ιδιότητες και εφαρμογές γεωπολυμερώνunclassified

Αξιοποίηση Ελληνικών Καολινών Στην Τεχνολογία Των Γεωπολυμερών

Tsitouras¹,

Τσιτούρας²

View full text Add to dashboard Cite

Το θέμα της διατριβής είναι η αξιοποίηση ελληνικών καολινών στην τεχνολογία των γεωπολυμερών. Ο γεωπολυμερισμός περιλαμβάνει χημική αντίδραση μεταξύ ενός αργιλοπυριτικού υλικού και ενός διαλύματος ενεργοποίησης υπό έντονα αλκαλικές συνθήκες. Τα προϊόντα του, είναι κυρίως άμορφα με βελτιωμένες ιδιότητες σε σχέση με συμβατικά υλικά.Στη διατριβή εξετάσθηκε ο γεωπολυμερισμός μετακαολινών από καολίνες με διαφοροποιημένη χημική και ορυκτολογική σύσταση. Αρχικά, μελετήθηκε η αλκαλική διαλυτοποίησή τους σε συνάρτηση με τη θερμοκρασία έψησης των καολινών και του αλκαλικού ιόντος. Στη συνέχεια, με την εφαρμογή ενός μοντέλου σχεδιασμού πειραμάτων Taguchi, έγινε αριστοποίηση των συνθηκών σύνθεσης με κριτήριο τη βελτιστοποίηση των αντοχών σε θλίψη. Τα προϊόντα χαρακτηρίστηκαν με XRD, FTIR και SEM. Τέλος, εξετάσθηκε η ανθεκτικότητα γεωπολυμερικών παστών και κονιαμάτων σε υψηλές θερμοκρασίες. Το εύρος διαλυτοποίησης εξαρτάται από τη σύσταση των καολινών, την κρυσταλλικότητα του καολινίτη, τη θερμοκρασία έψησης των καολινών και το είδος του αλκαλικού ιόντος. Μεγαλύτερο εύρος παρουσιάζεται σε διαλύματα NaOH, σε μετακαολίνες που έχουν παραχθεί με έψηση των καολινών στους 650°C.Ο γεωπολυμερισμός είναι πολύπλοκη διαδικασία, που επηρεάζεται από τη σύσταση της πρώτης ύλης και του διαλύματος ενεργοποίησης. Οι λόγοι Μ/Al, Na/(Na+K), [Si]/Μ2O (Μ: Na ή/και K) στο αρχικό μείγμα καθορίζουν τις ιδιότητες των γεωπολυμερών. Για όλους τους μετακαολίνες που μελετήθηκαν, ο παράγοντας με τη μεγαλύτερη συμβολή στην ανάπτυξη αντοχών είναι ο λόγος [Si]/M2O. Ακολουθεί ο λόγος M/Al, ενώ το είδος του αλκαλίου έχει οριακή επίδραση. Για σταθερές τιμές των παραπάνω παραμέτρων, η αύξηση του λόγου mστερεών/mυγρών προκαλεί σημαντική αύξηση των αντοχών.Τα γεωπολυμερή παρουσιάζουν αντοχές σε θλίψη έως 170 MPa και ενισχύονται ιδιαίτερα από την ύπαρξη χαλαζία ή/και χριστοβαλίτη στην πρώτη ύλη. Η προσθήκη ασβεστολιθικής άμμου μειώνει τις αντοχές στα κονιάματα ανάλογα με το ποσοστό της άμμου. Τα κονιάματα με αναλογία Άμμου/Μετακαολίνη = 3.0 διατηρούν το 30-55% των αντοχών των αντίστοιχων παστών.Τα γεωπολυμερή έχουν ικανοποιητική ανθεκτικότητα σε υψηλές θερμοκρασίες. Στους 600°C, oι γεωπολυμερικές πάστες διατηρούν έως το 55% των αντοχών τους, παρουσιάζοντας συρρίκνωση της τάξης του 8%, ενώ τα κονιάματα διατηρούν έως το 40% των αντοχών τους, παρουσιάζοντας συρρίκνωση της τάξης του 1%.Από τα παραπάνω προκύπτει ότι κοιτάσματα πτωχά σε καολινίτη μπορούν να αξιοποιηθούν στην τεχνολογία γεωπολυμερών.

show abstract

Effect of porosity on the absorbed, reemitted and transmitted light by a geopolymer metakaolin base

Cited by 20 publications

References 8 publications

Corrosion of Steel Rebars in Construction Materials with Reinforced Pervious Concrete

Corrosion of Steel Rebars in Construction Materials with Reinforced Pervious Concrete

Geopolymeric Composite Materials Made of Sol-Gel Silica and Agroindustrial Wastes of Rice, Barley, and Coffee Husks with Wood-Like Finishing

Αξιοποίηση Ελληνικών Καολινών Στην Τεχνολογία Των Γεωπολυμερών