Effect of plasmonic au nanoparticles on the photoactivity of polyaniline/indium tin oxide electrodes for water splitting

Abstract

Three nanomaterials based on polyaniline (PANI) are prepared on indium tin oxide (ITO) and applied as electrodes for H2 generation due to the water‐splitting process. PANI/ITO films are prepared using oxidation polymerization method at 25°C, then coated with Au nanoparticles with different thicknesses (sputter time from 1 to 2 min). The three prepared electrodes; PANI/ITO (Electrode (0), 1‐min‐Au/PANI/ITO (Electrode (I)), and 2‐min‐Au/PANI/ITO (Electrode (II)) are compared for H2 generation from H2O. Scanning electron microscope, X‐ray diffraction, UV‐Vis spectrophotometer, and Fourier‐transform infrared spectroscopy analyses have been carried out, in which the average PANI crystal size was ~20 nm. Moreover, the bandgaps were determined, in which 2‐min‐Au/PANI/ITO has the optimum bandgap of 2.25 eV. The characteristic behavior of the H2 generation took place depending on the current density (Jph) value by using Jph–V and Jph–time study. Also, the incident photon‐to‐current conversion efficiency (IPCE) and the applied bias photon‐to‐current efficiency (ABPE) were calculated for the Electrode (II) at 25°C. The optimum IPCE and ABPE efficiency were 18.7 and 0.99%, respectively, at 390 nm. By increasing the temperature to 70°C, the IPCE efficiency increases to about 37%. Finally, activation energy (Ea), enthalpy (ΔH*), and entropy (ΔS*) were determined, in which the values were 24.32 kJ mol−1, 10.90 kJ mol−1, and 74.99 J K−1 mol−1, respectively. © 2019 American Institute of Chemical Engineers Environ Prog, 38:e13146, 2019

Efficient photoselectrochemical hydrogen production utilizing of APbI 3 (A = Na, Cs, and Li) perovskites nanorods

“…Besides, most of the absorbed irradiation by the prepared nanostructured electrode from the artificial visible light generates a high density of electron-hole pairs, this matches our recently published literature. [47][48][49] The high value of the produced photocurrent density is an important indicator for successful PEC water splitting under 400 W halide lamp illumination.…”

Design of SnO2:Ni,Ir Nanoparticulate Photoelectrodes for Efficient Photoelectrochemical Water Splitting

“…The obtained results are also presented in Bode plots ( Figure 11 b,c). The Nyquist plot of 3.0% Ni-doped SnO 2 :Ir photoelectrode shows that there is a small semicircle with a small diameter in the high-f side, indicating the redox reaction [ 66 ], followed by a linear stage covering the region of middle/low fs. These PEC-IS spectra displayed mixed diffusion/kinetic controlled routes.…”

Nanoporous TiN/TiO2/Alumina Membrane for Photoelectrochemical Hydrogen Production from Sewage Water

“…After Au coating, the J ph value becomes stable at about 0.07 mA·cm −2 , Figure 9 b. These values indicate the TiN and Au coating materials have high stability and anticorrosion properties that maintain the produced J ph at the same values with time [ 13 , 61 ]. This means that every small change in the produced J ph value refers to a small corrosion reaction due to the acidity of the sewage water.…”

“…The most used plasmonic materials are noble metals, such as Au, Ru, Rh, and Pt, but these metals are very expensive [ 12 ]. Rabia et al used Au to enhance the water-splitting reaction for H 2 production under light [ 13 ]. Shi et al used Pt to enhance the activity of CdS materials for water splitting, in which the photoactivity is enhanced very much by using Pt metal [ 14 ].…”