Effect of Oligosaccharide Alcohol Addition to Alumina Slurry and Translucent Alumina Produced by Slip Casting

Abstract

A slurry used to produce dense green compacts by slip casting should exhibit low viscosity, high solids content, and good dispersion. Slurries with good characteristics were produced in the present study by adding oligosaccharide alcohol to an Al 2 O 3 slurry with an NH 4 ؉ salt of poly(methacrylic acid) (NH 4 ؉ -PMA). The role of NH 4 ؉ -PMA and oligosaccharide alcohol in the Al 2 O 3 slurry was examined by DTA, -potential measurement, high-pressure liquid chromatography, and viscometry. The viscosity of the slurry with NH 4 ؉ -PMA and oligosaccharide alcohol was lower than that of the slurry with NH 4 ؉ -PMA at a high solids content. Oligosaccharide alcohol did not interact with the Al 2 O 3 surface. However, the Al 2 O 3 slurry with NH 4 ؉ -PMA was influenced by the addition of oligosaccharide alcohol. We found that the dispersibility of the slurry was greatly improved by adding oligosaccharide alcohol. The transmittance of the Al 2 O 3 ceramics produced by slip casting using the slurry with both NH 4 ؉ -PMA and oligosaccharide alcohol was higher than that of ceramics produced by slip casting using the slurry with NH 4 ؉ -PMA alone. The increased optical property resulted from low viscosity, which was attributed to the addition of oligosaccharide alcohol, at a high solids content.

State of the Dispersant and Particle Surface During Wet‐Jet Milling for Preparation of a Stable Slurry

“…D ISPERSION of ceramic powders in a liquid phase is required in colloidal processing such as slip casting [1][2][3][4][5][6][7][8][9][10][11] and tape casting. [12][13][14][15] Colloidal processing has been shown to be superior to conventional dry pressing in terms of achieving higher density and sintered microstructure uniformity.…”

Effect of hot isostatically pressed sintering on microstructure of translucent alumina compact

“…For quantitative analysis, the relative density determined by the Archimedes method was taken into account because it could be linked with the desire physical strength and optical transmission [16][17][18]. These properties would be affected by the sintering parameters which are sintering temperature, atmosphere and time.…”

Preparation of translucent alumina ceramic specimen using slip casting method

“…An important issue to fabricate green body with high density is to control slurry viscosity while solid content with uniform dispersion must be controlled. 10), 11) Accordingly various dispersants have been investigated because they could suppress agglomeration of suspending particles by increasing the interparticle repulsive force. 12), 13) Meanwhile some binders are also added into ceramic slurry for improving strength of green body.…”