“…However, in this case, the alloy classes were analyzed separately, since there were more significant differences between the various steels and a common T i binning was not as useful. The data [4,7,20,22,26,27,[50][51][52][53][54][55][56][57][58][82][83][84][85][86][87][88][89][90][91][92][93][94][95][96], which in most cases were very scattered, could be reasonably fit using a simpler nonsaturating function • The ΔT c /Δσ y irradiations at T i < 400°C are generally less than the corresponding fracture toughness indexed ΔT o /Δσ y shifts. Thus the ΔT c from sub-sized Charpy tests are probably non-conservative, and may seriously underestimate the embrittlement potential of TMS.…”