Effect of Injected Oxygen Amount on the Gas Porosity and Mechanical Properties of a Pore-Free Die-Cast Al–Si–Cu Alloy

Abstract

With the rise in the demand for eco-friendly and electric vehicles, welding and heat treatment are becoming very important to meet the necessary weight reduction, complexity, and high functionality of die castings. Pore-free (PF) die casting is an effective process that enables heat treatment and welding due to low gas porosities. Indeed, this process affords castings of low gas porosity, similar to those attained by high-vacuum die casting. In this study, we compared the gas porosities of different castings fabricated by PF die casting using varied injected oxygen amounts. The castings were all subjected to T6 heat treatment and analyzed by computed tomography (CT) to compare their microstructure and mechanical properties before and after T6 heat treatment. The results revealed that with the increasing injected oxygen amount, the gas porosity of the specimens decreased while their mechanical properties increased. In particular, the gas porosity was the lowest at 1.26 L. Moreover, the 1.26 L specimen displayed the best tensile strength, yield strength, and elongation results. Finally, Weibull distribution analysis revealed that the tensile strength and elongation repeatability and reproducibility increased with increasing injected oxygen amount.

Microstructural and mechanical characterization of additively manufactured parts of maraging 18Ni300M steel with water and gas atomized powders feedstock

“…In this scenario, pores are formed because gases exhibit higher solubility in liquids than in solids. As the metal solidifies, the gas concentration in the liquid increases until gas bubbles are formed, subsequently giving rise to gas porosity [42,[44][45][46][47][48].…”

Joining Technologies for Aluminium Castings—A Review

“…Pore-free die casting [22] Effectively reduce blow hole, dense microstructures and fine grains Complex process, easy form oxide inclusions and high production cost…”