Effect of Ammonium Polyacrylate and Pre-Oxidation on Rheological Properties of Si₃N₄ Slurries

Abstract

The key for gel-casting is the preparation of ceramic aqueous slurries with excellent rheological properties. The effect of ammonium polyacrylate and pre-oxidation on rheological properties of Si3N4 slurries was investigated. The Si3N4 isoelectric point (IEP) is between 3 and 4 in premix solution and particle surface potential is maximum at pH between 9.5 and 10.5. PAA-NH4 of dispersant can obviously decrease the viscosity of Si3N4 slurries, and the optimal dosage is about 1.6wt% of Si3N4 powders. Meanwhile, the Si3N4 slurries exhibit pseudoplastic fluid with the characteristic of shear-thinning behavior. Due to the improvement of powder surface characteristic, the pre-oxidation significantly improve the rheological properties of the Si3N4 slurries.

Fabrication and characterization of Si 3 N 4 whisker‐reinforced SiO 2 ceramic for radome materials

“…Moreover, the slurry stability of adding the pre‐oxidized whiskers is better than that of the untreated slurry as a result of the excellent hydrophilic of an exterior SiO 2 . In addition, the viscosity of the slurry, including pre‐oxidized Si 3 N 4 whiskers dramatically drops 16 . Therefore, it is vital to figure out the oxidation behaviors of Si 3 N 4 whiskers before the groundwork of the Si 3 N 4w /SiO 2 slurry.…”

“…In addition, the viscosity of the slurry, including pre-oxidized Si 3 N 4 whiskers dramatically drops. 16 Therefore, it is vital to figure out the oxidation behaviors of Si 3 N 4 whiskers before the groundwork of the Si 3 N 4w /SiO 2 slurry.…”

Fonksiyonel Derecelendirilmiş Si₃N₄ Esaslı Seramiklerin Üretiminde Farklı Soğuk İzostatik Pres (CIP) Basınçlarının Etkisinin İncelenmesi

“…Soğuk izostatik pres (CIP) genelde su ve yağ karışımının basıncıyla birlikte numunenin bir kauçuk kalıp içine alınıp eşit şekilde preslendiği bir yöntemdir, 20MPa ila 1 GPa arasında değişen çeşitli basınç parametresine sahiptir [16,23]. Silisyum nitrür şeritlerinin üretiminde kolloidal sistem ve özellikle bağlayıcı/plastikleştirici/katı yükü/dağıtıcı miktarı ve özellikleri önem arz etmektedir, çalışmamızda solvent bazlı bir sistem kullanılmıştır [4,5,10,24]. Şekillendirilen parçalara bağlayıcı giderme işlemi uygulanmış olup ardından hava ortamında sinterleme işlemi yapılmıştır.…”