Effect of AlSiFe on the anodizing process of 6063 aluminum

Abstract

AlSiFe phase can form microscopic galvanic couples that decrease corrosion resistance of 6063 aluminum which may influence the anodizing process. Two samples of 6063 aluminum were prepared. One sample was cut along the extrusion direction of the billet, and the other was cut perpendicular to the extrusion direction. Both samples exhibited the same characteristics, except for the distribution of the second phase AlSiFe. Both samples were subjected to anodizing treatments. Comparison between anodic oxide films was performed. The microstructure of Al substrates and anodic oxide films were examined using a scanning electron microscope, an optical microscope, and a glow discharge optical emission spectrometer. Results indicated that the thicknesses and elemental distributions of the anodic oxide films were almost the same. Moreover, the second phase AlSiFe influenced the anodic oxidation process, resulting in cavities in the anodic oxide film that affected its brightness. Copyright © 2016 John Wiley & Sons, Ltd.

A Review of Research on Galvanic Corrosion of Aluminum Alloys

“…According to the different preparation methods, the anodic alumina (AAO) membrane can be divided into two types: barrier type and multi-pass type [71]. It should be noted that the temperature and pH of the electrolyte should be kept within a small range during the anodic oxidation process; otherwise, the pore shape, geometric size and stack thickness on the surface will be distributed unevenly [72]. On the original basis, micro-arc oxidation (MAO) technology can generate ceramic oxide film on aluminum alloy through arc light discharge, which has better wear resistance and corrosion resistance [73].…”

Formation Mechanism of Strip Defects in Anodizing AA5252 Aluminium Alloy Sheets

“…Previous researches [3][4][5] indicated that the strip defects not only correlate strongly with the anodizing conditions (voltage, temperature, composition and acid concentration of the bath), but also depend on the microstructure of the aluminium substrate, i.e. impurity distribution, grain size, texture and surface morphology.…”