EBSD of Zn-rich phases in Zn–Al-based alloys

Zhu, Yao; Lee, Wing Bun; Yeung, C. F.; Yue, Tai Man

doi:10.1016/s1044-5803(00)00088-7

Cited by 15 publications

(6 citation statements)

References 5 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Estudos anteriores identificaram a transformação da fase metaestável ε na fase estável τ durante o tratamento térmico de solubilização a 150ºC por 145 horas. (Zhu et al, 2001). Esta transformação de fases tem sido identificada em tratamentos térmicos abaixo de 250ºC.…”

Section: Tratamentos Térmicosunclassified

“…Pode-se observar (FIGURA 11) que na liga Zamac 8 modificada com adição de 8% de cobre após tratamento térmico a 150 °C formaram-se partículas nas bordas das dendritas primárias, muito similar ao observado por Zhu et al (2001) para uma liga ternária de Zn85A4Cu11. Zhu et al (2001) mostraram que a decomposição da fase ε leva a precipitação fase τ nas bordas da estrutura globular da fase primária após tratamento térmico realizado a 150 °C por 145 h. Já no caso da liga tratamento térmico a 300 °C (FIGURA 12) observa-se a concentração de partículas nas dendritas da fase primária, indicando que há uma temperatura ideal para realização de tratamento térmico com a finalidade de estabilizar a liga pela transformação da fase ε.…”

Section: A)unclassified

See 1 more Smart Citation

Ligas De Zinco-Alumínio Hipoeutéticas: Efeito Do Cobre E Tratamento Térmico Na Microestrutura

Silva

Costa²

2017

Destaques Acadêmicos

View full text Add to dashboard Cite

Neste trabalho estuda-se a influência da adição de cobre e de tratamento térmico na microestrutura da liga Zamac 8 comercial (ZnAl4Cu2,6Mg0,5). Para tal, duas ligas foram fundidas, a liga zamac 8 e a liga zamac 8 com adição de 8% em peso de cobre, sendo que a solidificação foi acompanhada por análise térmica. O tratamento térmico foi realizado em duas condições: a 150 C 143 h e a 300 C por 94 h. A caracterização das ligas antes e após a realização do tratamento térmico foram realizadas por microscopia eletrônica de varredura e mapeamento por EDS (Energy Dispersive X-Ray Spectroscopy) e por medidas de dureza Brinell. A adição de cobre levou a um aumento no intervalo de solidificação da liga Zamac 8 comercial e alterou o tempo da formação de cada fase/microconstituinte, levando à variação entre as quantidades relativas de cada fase ou microconstituinte. Os tratamentos térmicos alteraram a microestrutura, tanto da liga comercial quanto da liga modificada pela adição de cobre. Para a liga Zamac 8 comercial o tratamento térmico realizado a 300 C por 94 h foi o que promoveu a diminuição partículas da fase presentes nas dendritas da fase, enquanto que para a liga Zamac 8 com adição de Cobre foi o tratamento térmico realizado a 150 C por 143 h. No entanto, o mapeamento por EDS mostra que há cobre em maior concentração na fase primária independente da temperatura e tempo de tratamento térmico, indicando que pode ter havido transformação da fase metaestável na fase estável , que também contém cobre. Não foi verificado alteração significativa na dureza do material após tratamento térmico, exceto na liga comercial Zamac 8 tratada termicamente a 150 C por 94 horas, esta alteração pode ser explicada pela microestrutura, onde o percentual da estrutura eutética presente é baixo.

show abstract

Section: Tratamentos Térmicosunclassified

Section: A)unclassified

Ligas De Zinco-Alumínio Hipoeutéticas: Efeito Do Cobre E Tratamento Térmico Na Microestrutura

Silva

Costa²

2017

Destaques Acadêmicos

View full text Add to dashboard Cite

show abstract

“…In these works the OIM-EBSD technique was used to determine phases that are present in the alloy (Zhu et al, 2001) as well as a complementary technique in the study of microstructural changes on as casting or extruded and subsequently solubilized Zn-Al alloys (Zhu et al, 2001(Zhu et al, , 2003. In these works the OIM-EBSD technique was used to determine phases that are present in the alloy (Zhu et al, 2001) as well as a complementary technique in the study of microstructural changes on as casting or extruded and subsequently solubilized Zn-Al alloys (Zhu et al, 2001(Zhu et al, , 2003.…”

Section: Introductionmentioning

confidence: 99%

“…Some Zn-Al-based alloys have been studied using EBSD. In these works the OIM-EBSD technique was used to determine phases that are present in the alloy (Zhu et al, 2001) as well as a complementary technique in the study of microstructural changes on as casting or extruded and subsequently solubilized Zn-Al alloys (Zhu et al, 2001(Zhu et al, , 2003. In these studies mechanical polishing with diamond pastes of 6 and 4 µm were made and EBSPs were obtained, however, in the discussion of the phase maps, the authors indicated that there were large areas that could not be indexed.…”

Section: Introductionmentioning

confidence: 99%

Metallographic Preparation of Zn-21Al-2Cu Alloy for Analysis by Electron Backscatter Diffraction (EBSD)

et al. 2014

View full text Add to dashboard Cite

Samples of Zn-21Al-2Cu alloy (Zinalco) that will be heavily deformed were prepared using five different manual mechanical metallographic methods. Samples were analyzed before tensile testing using the orientation imaging microscopy-electron backscatter diffraction (OIM-EBSD) technique. The effect of type and particle size during the final polishing stages for this material were studied in order to identify a method that produces a flat, damage free surface with a roughness of about 50 nm and clean from oxide layers, thereby producing diffraction patterns with high image quality (IQ) and adequate confidence indexes (CI). Our results show that final polishing with alumina and silica, as was previously suggested by other research groups for alloys that are difficult to prepare or alloys with low melting point, are not suitable for manual metallographic preparation of this alloy. Indexes of IQ and CI can be used to evaluate methods of metallographic preparation of samples studied using the OIM-EBSD technique.

show abstract

“…Also, it is being increasingly used for crystal structure determination and phase identification and transformations (Gourgues‐Lorenzon, 2007). In our previous studies, EBSD was used for the identification of crystal and quasicrystal phases (Zhu et al , 2001, 2003b; Cheung et al ., 2001; To et al 2007) and external stress induced phase transformations (Zhu et al , 2003a).…”

Section: Introductionmentioning

confidence: 99%

Use of EBSD to study electropulsing induced reverse phase transformations in a Zn-Al alloy (ZA22)

Zhu

Liu

2010

Journal of Microscopy

View full text Add to dashboard Cite

SummaryMulti-phase identification and phase transformations in electropulsing treated Zn-Al based alloy wire specimens were studied using electron back-scattered diffraction, backscattered scanning electron microscopy and X-ray diffraction techniques. By using electron back-scattered diffraction, two phases: η S and η T with a small difference of about 1% in lattice parameters (c 0 /a 0 ) were identified, based on the determined lattice parameters of the phases, and the reverse eutectoid phase transformations: η T + ε T + α T → η S and ε + α → T + η were successfully detected. Electron back-scattered diffraction appeared to be an effective technique for studying complex electropulsing induced phase transformations.

show abstract

EBSD of Zn-rich phases in Zn–Al-based alloys

Cited by 15 publications

References 5 publications

Ligas De Zinco-Alumínio Hipoeutéticas: Efeito Do Cobre E Tratamento Térmico Na Microestrutura

Ligas De Zinco-Alumínio Hipoeutéticas: Efeito Do Cobre E Tratamento Térmico Na Microestrutura

Metallographic Preparation of Zn-21Al-2Cu Alloy for Analysis by Electron Backscatter Diffraction (EBSD)

Use of EBSD to study electropulsing induced reverse phase transformations in a Zn-Al alloy (ZA22)

Contact Info

Product

Resources

About