We have fabricated multifunctional conductive fabrics composed of polypyrrole/BaTiO3/poly(acrylonitrile‐co‐methylacrylate) (PPy/BaTiO3/P(AN‐co‐MA)(PBA) utilizing a simple process including dip coating and in situ chemical polymerization of pyrrole, which oxidized both ammonium persulfate (APS) and ammonium persulfate + iron (III) chloride (APS + FeCl3) for flexible and wearable textile applications. The influence of the oxidant nature, PPy content, and BaTiO3 on the surface structures, electrochemical, and semiconducting characteristics of the fabrics was examined using scanning electrochemical microscopy (SEM), electrochemical impedance spectroscopy (EIS), and the Mott–Schottky (M–S) studies. The study revealed that the size of the polymer nanostructures on fabric has an impact on the electrochemical impedance properties. Specifically, a decrease in diameter (when FeCl3 + APS is used) or the formation of more compact swelling surface structures (when only APS is used) is associated with changes in the conductivity of the coated fabric. Based on the EIS tests, the composite coating (S0.1, S0.2, and S0.3) with FeCl3 has a higher electrical conductivity compared to the coating with APS (PBA). The M–S tests indicate that the semiconducting characteristics of coated fabrics are dependent upon the kind of oxidant, the amount of PPy, and the presence of BaTiO3.
We have fabricated multifunctional conductive fabrics composed of polypyrrole/BaTiO3/poly(acrylonitrile‐co‐methylacrylate) (PPy/BaTiO3/P(AN‐co‐MA)(PBA) utilizing a simple process including dip coating and in situ chemical polymerization of pyrrole, which oxidized both ammonium persulfate (APS) and ammonium persulfate + iron (III) chloride (APS + FeCl3) for flexible and wearable textile applications. The influence of the oxidant nature, PPy content, and BaTiO3 on the surface structures, electrochemical, and semiconducting characteristics of the fabrics was examined using scanning electrochemical microscopy (SEM), electrochemical impedance spectroscopy (EIS), and the Mott–Schottky (M–S) studies. The study revealed that the size of the polymer nanostructures on fabric has an impact on the electrochemical impedance properties. Specifically, a decrease in diameter (when FeCl3 + APS is used) or the formation of more compact swelling surface structures (when only APS is used) is associated with changes in the conductivity of the coated fabric. Based on the EIS tests, the composite coating (S0.1, S0.2, and S0.3) with FeCl3 has a higher electrical conductivity compared to the coating with APS (PBA). The M–S tests indicate that the semiconducting characteristics of coated fabrics are dependent upon the kind of oxidant, the amount of PPy, and the presence of BaTiO3.
Worldwide, there is growing concern over the toxicity of arsenic in drinking water. The US Environmental Protection Agency and Central Pollution Control Board (India) have set a safe limit of 50 parts per billion for arsenic in drinking water. Millions of people are at immediate risk due to high concentrations of arsenic in drinking water, particularly in developing nations where arsenic poisoning symptoms have been observed. One of the essential techniques described in this article is the absorption of arsenic from contaminated water by sustainable cellulosic materials like jute and wood sawdust after suitable modification. Jute and sawdust are cheap and abundantly available in South Asia. They are functionalized with polypyrrole coating by in situ chemical polymerization of pyrrole in aqueous medium in the presence of ferric chloride. Polypyrrole-coated jute fabric (with 11.28% polypyrrole add-on) and polypyrrole-coated sawdust (with 5.28% polypyrrole add-on) are found to be excellent adsorbers of arsenic ion (As3+) from water. The effect of dosage of polypyrrole-coated adsorbents, treatment time and pyrrole concentration on the As removal efficiency have been investigated in this work. The arsenic concentration in water is determined using a microwave plasma atomic emission spectrometer with the highest level of accuracy. Maximum As removal efficiency by the polypyrrole-coated sawdust and polypyrrole-coated jute fabric is found to be 80.90% and 97.3%, respectively, from a 50 mL, 7.5 parts per million As solution with a dosage of 1 g at neutral pH. The polypyrrole-coated jute and sawdust are characterized by Fourier-transform infrared spectroscopy to understand the chemical interaction between cellulose and polypyrrole molecules. The scanning electron microscope studies reveal a uniform coating of polypyrrole around the surface of jute fibre and sawdust particles. Thermo-gravimetric analysis shows good thermal stability of jute and sawdust after polypyrrole coating.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.