Development of Manufacturing Process of Pure Titanium Wire to make Eyewear Frame

Abstract

After pure titanium Ingot(G2) with 400mm in diameter was manufactured, the analysis of its ingredients showed that the oxygen content was 0.073wt% and the iron content was 0.03wt%, which made ASTM Gr.2 standardization satisfactory. The processed titanium ingot produced 42mm wire rod, and hot rolling of 18th phase produced 9mm wire rod. The hardness analysis of 15.8mm wire rod, which was processed in hot rolling of 10th phase from the surface to the center, resulted in almost constant value with Hv150~200. The last 9mm wire rod had a different yield strength and elongation percentage depending on the temperature as it was led in to a hot roller. However, tensile strength revealed an approximate value and made ASTM B863 standardization satisfactory.